Polyborosilazane preceramic as matrix resin of high temperature adhesive for graphite bonding

	Polyborosilazane preceramic as matrix resin of high temperature adhesive for graphite bonding
	Li, Shuqin 1; Luo, Yongming 2; Wang, Linhao 2; Xu, Caihong 2
刊名	INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY
	2017-09-01
卷号	14 期号:5 页码:999-1005
关键词	Heat Treatment High Temperature Adhesives Joining Mechanical Properties Of Adhesives
英文摘要	In this study, a modified high temperature adhesive based on polyborosilazane preceramic was developed for joining graphite. The properties of adhesive as well as bonding performance of both directly cured joints and calcined joints were investigated. The results showed that the shear strength reached the highest value 13.6MPa after calcination at 1100 degrees C due to the formation of heat-resistant ceramic phases and solidification of molten species during joining process. Besides, the compressive shear strength of cured adhesive without posttreatment was kept above 6MPa during test from RT to 1100 degrees C, which made it possible applied directly in practical high temperature environment.
语种	英语
内容类型	期刊论文
源URL	[http://ir.iccas.ac.cn/handle/121111/39258]
专题	化学研究所_高技术材料实验室
作者单位	1.China Aerosp Sci & Ind Corp, Inst 306, Beijing, Peoples R China 2.Chinese Acad Sci, Inst Chem, Beijing, Peoples R China
推荐引用方式 GB/T 7714	Li, Shuqin,Luo, Yongming,Wang, Linhao,et al. Polyborosilazane preceramic as matrix resin of high temperature adhesive for graphite bonding[J]. INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,2017,14(5):999-1005.
APA	Li, Shuqin,Luo, Yongming,Wang, Linhao,&Xu, Caihong.(2017).Polyborosilazane preceramic as matrix resin of high temperature adhesive for graphite bonding.INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,14(5),999-1005.
MLA	Li, Shuqin,et al."Polyborosilazane preceramic as matrix resin of high temperature adhesive for graphite bonding".INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY 14.5(2017):999-1005.