Creep behavior and lifetime prediction of PMMA immersed in liquid scintillator | |
Zhou, F; Hou SJ(侯少静)![]() ![]() | |
刊名 | POLYMER TESTING
![]() |
2016 | |
卷号 | 53页码:323 |
关键词 | Creep PMMA Time-Stress Superposition Principle Master curve Lifetime prediction |
DOI | 10.1016/j.polymertesting.2016.06.016 |
文献子类 | Article |
英文摘要 | The creep behavior of PMMA immersed in liquid scintillator at room temperature was experimentally studied with a new type of creep test machine. Both short-term and creep-rupture tensile tests at eight stress levels were performed. A master curve of creep compliance at a reference stress was obtained according to the Time-Stress Superposition Principle. The master curve was compared with the actual long-term creep curve. It demonstrates that the two curves coincide well at short times. However, the actual creep data shows a higher creep rate as time goes on. The actual lifetime is much shorter than that predicted by the master curve. Furthermore, the relationship between long-term creep limited strength and service life was determined. The results can be used to guide the safety design of PMMA vessels for application in a neutrino observatory. (C) 2016 Elsevier Ltd. All rights reserved. |
WOS关键词 | NONLINEAR VISCOELASTIC MATERIALS ; TIME-TEMPERATURE ; POLY(METHYL METHACRYLATE) ; STRESS ; POLYCARBONATE ; SUPERPOSITION ; COMPOSITES ; PRINCIPLE ; RUPTURE |
语种 | 英语 |
WOS记录号 | WOS:000380628800041 |
内容类型 | 期刊论文 |
源URL | [http://ir.ihep.ac.cn/handle/311005/260869] ![]() |
专题 | 高能物理研究所_实验物理中心 |
作者单位 | 中国科学院高能物理研究所 |
推荐引用方式 GB/T 7714 | Zhou, F,Hou SJ,Qian XH,et al. Creep behavior and lifetime prediction of PMMA immersed in liquid scintillator[J]. POLYMER TESTING,2016,53:323. |
APA | Zhou, F.,侯少静.,钱小辉.,Hou, SJ.,Qian, XH.,...&Xu, F.(2016).Creep behavior and lifetime prediction of PMMA immersed in liquid scintillator.POLYMER TESTING,53,323. |
MLA | Zhou, F,et al."Creep behavior and lifetime prediction of PMMA immersed in liquid scintillator".POLYMER TESTING 53(2016):323. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论