Microstructure and Microhardness of Laser Metal Deposition Shaping K465/Stellite-6 Laminated Material | |
Zhao JB(赵吉宾)![]() ![]() | |
刊名 | METALS
![]() |
2017 | |
卷号 | 7期号:11页码:1-10 |
关键词 | laser metal deposition shaping laminated material microstructure microhardness |
ISSN号 | 2075-4701 |
通讯作者 | Wang ZG(王志国) |
产权排序 | 1 |
中文摘要 | K465 superalloy with high titanium and aluminum contents was easy to crack during laser metal deposition. In this study, the crack-free sample of K465/Stellite-6 laminated material was formed by laser metal deposition shaping to control the cracking behaviour in laser metal deposition of K465 superalloy. The microstructure differences between the K465 superalloy with cracking and the laminated material were discussed. The microstructure and intermetallic phases were analyzed through scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD). The results showed that the microstructure of K465/Stellite-6 laminated material samples consisted of continuous dendrites with a similar structure size in different alloy deposition layers, and the second dendrite arm spacing was finer compared with laser metal deposition shaping K465. The intermetallic phases in the different alloy deposition layers varied, and the volume fraction of carbides in K465 deposition layer of the laminated material was higher than only K465 deposition under the fluid flow effect. In addition, the composition and microhardness distribution of laminated materials variation occurred along the deposition direction. |
WOS标题词 | Science & Technology ; Technology |
类目[WOS] | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
研究领域[WOS] | Materials Science ; Metallurgy & Metallurgical Engineering |
关键词[WOS] | HEAT-AFFECTED ZONE ; LIQUATION CRACKING ; K465 SUPERALLOY ; ALLOY ; RESISTANCE ; BEHAVIOR ; STEEL |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000416803200062 |
内容类型 | 期刊论文 |
源URL | [http://ir.sia.cn/handle/173321/21391] ![]() |
专题 | 沈阳自动化研究所_装备制造技术研究室 |
作者单位 | 1.Superalloys Division, Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Road, Shenyang 110016, China 2.Equipment Manufacturing Technology Research Laboratory, Shenyang Institute of Automation, Chinese Academy of Sciences, Shenyang 110016, China |
推荐引用方式 GB/T 7714 | Zhao JB,Wang ZG,Shi F,et al. Microstructure and Microhardness of Laser Metal Deposition Shaping K465/Stellite-6 Laminated Material[J]. METALS,2017,7(11):1-10. |
APA | Zhao JB,Wang ZG,Shi F,Zhang, Hongyu,&Zhao YH.(2017).Microstructure and Microhardness of Laser Metal Deposition Shaping K465/Stellite-6 Laminated Material.METALS,7(11),1-10. |
MLA | Zhao JB,et al."Microstructure and Microhardness of Laser Metal Deposition Shaping K465/Stellite-6 Laminated Material".METALS 7.11(2017):1-10. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论