Effect of thickness on the electrical and optical properties of epitaxial (La0.07Ba0.93)SnO3 thin films | |
Liu, Qinzhuang1; Jin, Feng2; Dai, Jianming3; Li, Bing1; Geng, Lei1; Liu, Jianjun1 | |
刊名 | SUPERLATTICES AND MICROSTRUCTURES
![]() |
2016-08-01 | |
卷号 | 96期号:无页码:205-211 |
关键词 | Thin Films Transport Properties Optical Properties Alkaline Earth Stannate Pulsed Laser Deposition |
DOI | 10.1016/j.spmi.2016.05.027 |
文献子类 | Article |
英文摘要 | Transparent conductive oxide (La0.07Ba0.93)SnO3 (LBSO) thin films with thickness ranged from 220 nm to 11 nm were epitaxially grown on MgO substrate by pulsed laser deposition. The effect of thickness on the structural, transport, and optical properties of LBSO thin films was investigated in detail. With the film thickness decreasing, x-ray diffraction characterizations show that the LBSO (002) diffraction peak has no obvious shift, but the values of the full width at half maximum increase gradually from 0.608 degrees to 1.136 degrees due to the deterioration of crystalline quality of LBSO films. Atomic force microcopy reveals that the root-mean-square surface roughness of LBSO films decreases from 3.93 to 0.268 nm with film thickness decreasing. The lowest resistivity value of 1.181 x 10(-4) Omega cm at room temperature was observed in 220 nm thick films, with the highest carrier mobility of 41.06 cm(2) V-1 s(-1) and carrier concentration of 8.377 x 10(20) cm(-3). Furthermore, the resistivity increases gradually with the decrease of LBSO film thickness. Temperature dependent resistivity measurements indicate that the metal-semiconductor transition temperature of LBSO thin film changes regularly with the film thickness. The optical band gap of LBSO thin film decreases from 4.58 to 3.55 eV with decreasing the thickness, which was explained by the Burstein-Moss effect. (C) 2016 Elsevier Ltd. All rights reserved. |
WOS关键词 | TRANSPORT-PROPERTIES ; OXIDE ; TRANSITION ; METAL ; TIO2 |
WOS研究方向 | Physics |
语种 | 英语 |
WOS记录号 | WOS:000383308700023 |
资助机构 | Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; 11504120) ; 11504120) ; 11504120) ; 11504120) ; 11504120) ; 11504120) ; 11504120) ; 11504120) ; 1608085QE90) ; 1608085QE90) ; 1608085QE90) ; 1608085QE90) ; 1608085QE90) ; 1608085QE90) ; 1608085QE90) ; 1608085QE90) ; Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Chinese Natural Science Foundation(11374304 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Province(1408085QA19 ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Natural Science Foundation of Anhui Higher Education Institutions of China(KJ2015A095) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Foundation of the Anhui Provincial Education Department for Outstanding Young Talents in University(gxyqZD2016110) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; Collaborative Innovation Center of Advanced Functional Materials(XTZX103732015012) ; 11504120) ; 11504120) ; 11504120) ; 11504120) ; 11504120) ; 11504120) ; 11504120) ; 11504120) ; 1608085QE90) ; 1608085QE90) ; 1608085QE90) ; 1608085QE90) ; 1608085QE90) ; 1608085QE90) ; 1608085QE90) ; 1608085QE90) |
内容类型 | 期刊论文 |
源URL | [http://ir.hfcas.ac.cn:8080/handle/334002/22051] ![]() |
专题 | 合肥物质科学研究院_中科院固体物理研究所 |
作者单位 | 1.Huaibei Normal Univ, Sch Phys & Elect Informat, Huaibei 235000, Peoples R China 2.Univ Sci & Technol China, Hefei Natl Lab Phys Sci Microscale, Hefei 230026, Peoples R China 3.Chinese Acad Sci, Inst Solid State Phys, Hefei 230031, Peoples R China |
推荐引用方式 GB/T 7714 | Liu, Qinzhuang,Jin, Feng,Dai, Jianming,et al. Effect of thickness on the electrical and optical properties of epitaxial (La0.07Ba0.93)SnO3 thin films[J]. SUPERLATTICES AND MICROSTRUCTURES,2016,96(无):205-211. |
APA | Liu, Qinzhuang,Jin, Feng,Dai, Jianming,Li, Bing,Geng, Lei,&Liu, Jianjun.(2016).Effect of thickness on the electrical and optical properties of epitaxial (La0.07Ba0.93)SnO3 thin films.SUPERLATTICES AND MICROSTRUCTURES,96(无),205-211. |
MLA | Liu, Qinzhuang,et al."Effect of thickness on the electrical and optical properties of epitaxial (La0.07Ba0.93)SnO3 thin films".SUPERLATTICES AND MICROSTRUCTURES 96.无(2016):205-211. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论