Conductor Performance of CCCN3, CCCN4, and CCCN5 Samples for ITER CC Coils | |
Liu, Bo1; Wu, Yu1; Qin, Jing-Gang1; Devred, Arnaud2; Bruzzone, Pierluigi3; Stepanov, Boris3; Sedlak, Kamil3; Long, Feng1; Liu, Hua-Jun1; Liu, Fang1 | |
刊名 | IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY |
2016-06-01 | |
卷号 | 26期号:4页码:4802204 |
关键词 | Ac Loss Cc Conductor Iter Nbti T-cs |
DOI | 10.1109/TASC.2016.2535660 |
文献子类 | Article |
英文摘要 | The conductor for the ITER correction coils (CCs) is manufactured in China and is tested in the SULTAN facility. The third China CC conductor for the qualification SULTAN test sample (CCCN3) was prepared from a 200-m-long CC conductor unit length (Phase II). The fourth and fifth China CC conductor samples for SULTAN testing (CCCN4 and CCCN5) were prepared from the 576-m-long production unit lengths (Phase III). The current sharing temperature T-cs test results show that the sections of CCCN3, CCCN4, and CCCN5 have high T-cs performance. Using the electrical method, the T-cs was 7.13 K for CCCN3, 7.10 K for CCCN4, and 7.09 K for CCCN5 at the ITER reference test conditions, i.e., at B-sultan = 3.7 T and current equal to 10 kA (B-peak = 4.0 T). Even after the 2000 electromagnetic load cycles for CCCN3 conductor and 1000 electromagnetic load cycles for CCCN4 and CCCN5, the T-cs performance of all samples did not changed appreciably. Based on the CC conductor sample test results at 10 kA and at different fields, the T-cs was extrapolated to the peak field B-peak = 4.1 T and current equal to 10 kA. The extrapolated T-cs is 7.07 K for CCCN3, 7.05 K for CCCN4, and 7.03 K for CCCN5. The T-cs performance for all conductors is higher than the ITER acceptance criteria of 7.00 K. |
WOS研究方向 | Engineering ; Physics |
语种 | 英语 |
WOS记录号 | WOS:000373115700001 |
内容类型 | 期刊论文 |
源URL | [http://ir.hfcas.ac.cn:8080/handle/334002/21704] |
专题 | 合肥物质科学研究院_中科院等离子体物理研究所 |
作者单位 | 1.Chinese Acad Sci, Inst Plasma Phys, Hefei 230031, Peoples R China 2.ITER Org, F-13115 St Paul Les Durance, France 3.EPFL, Swiss Plasma Ctr, CH-5232 Villigen, Switzerland |
推荐引用方式 GB/T 7714 | Liu, Bo,Wu, Yu,Qin, Jing-Gang,et al. Conductor Performance of CCCN3, CCCN4, and CCCN5 Samples for ITER CC Coils[J]. IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY,2016,26(4):4802204. |
APA | Liu, Bo.,Wu, Yu.,Qin, Jing-Gang.,Devred, Arnaud.,Bruzzone, Pierluigi.,...&Yu, Min.(2016).Conductor Performance of CCCN3, CCCN4, and CCCN5 Samples for ITER CC Coils.IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY,26(4),4802204. |
MLA | Liu, Bo,et al."Conductor Performance of CCCN3, CCCN4, and CCCN5 Samples for ITER CC Coils".IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY 26.4(2016):4802204. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论