Crystal growth, polarized spectra, and laser performance of Yb:CaGdAlO4 crystal | |
Xu, X. D.; Di, J. Q.; Xia, C. T.; Zheng, L. H.; Aka, G.; Yu, H. H.; Sai, Q. L.; Guo, X. Y.; Zhu, L. | |
刊名 | Laser Phys.
![]() |
2016 | |
卷号 | 26期号:4 |
通讯作者 | jvqing.di@vitalchem.com ; xdxu79@mail.sic.ac.cn ; xia_ct@siom.ac.cn |
英文摘要 | In this paper, the crystal growth, polarized spectra, and laser performance of Yb:CaGdAlO4 crystal were reported. The segregation coefficient of Yb3+ ions was calculated to be 0.47. The cell parameters were determined to be a = b = 0.3658 nm, c = 1.1985 nm. The peak absorption cross-section was calculated to be 2.65 x 10(-20) cm(2) at 979 nm and the peak stimulated emission cross-section was 2.23 x 10(-20) cm(2) at 980 nm for the p polarization. The continuous-wave (CW) laser operations of uncoated Yb:CaGdAlO4 crystals with 5 x 5 x 3 mm(3) in size were demonstrated. A maximum output power of 1.6 W at 1048 nm was obtained with a slope efficiency of 28%. The results show that Yb: CaGdAlO4 crystal is a promising laser medium. |
收录类别 | SCI |
资助信息 | Yang Fan Project of Guangdong, Science and Technology Commission of Shanghai Municipality [13111103700]; Natural Science Foundation of Shanghai [15ZR1444700] |
WOS记录号 | WOS:000375157900018 |
内容类型 | 期刊论文 |
源URL | [http://ir.siom.ac.cn/handle/181231/28043] ![]() |
专题 | 上海光学精密机械研究所_中科院强激光材料重点实验室 |
作者单位 | 中国科学院上海光学精密机械研究所 |
推荐引用方式 GB/T 7714 | Xu, X. D.,Di, J. Q.,Xia, C. T.,et al. Crystal growth, polarized spectra, and laser performance of Yb:CaGdAlO4 crystal[J]. Laser Phys.,2016,26(4). |
APA | Xu, X. D..,Di, J. Q..,Xia, C. T..,Zheng, L. H..,Aka, G..,...&Zhu, L..(2016).Crystal growth, polarized spectra, and laser performance of Yb:CaGdAlO4 crystal.Laser Phys.,26(4). |
MLA | Xu, X. D.,et al."Crystal growth, polarized spectra, and laser performance of Yb:CaGdAlO4 crystal".Laser Phys. 26.4(2016). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论