Luminescence and scintillation response of Ce3+-doped oxide glasses with high Gd2O3content | |
Babin, Vladimir; Lertloypanyachai, Prapon; Pattanaboonmee, Nakarin; Chewpraditkul, Weerapong; Chen, Danping; Nikl, Martin | |
2016 | |
英文摘要 | This report presents the luminescence and scintillation response of Ce3+-doped oxide glasses with high Gd2O3(30 mol%) content. The characteristic emission of Ce3+5d → 4f transition peaking around 380 nm was observed in its luminescence spectra under UV and X-ray excitation. Photoluminescence decay kinetics was governed by a few tens of nanoseconds decay time. The integral scintillation efficiency of about 22% of that of the Bi4Ge3O12scintillator was obtained under X-ray irradiation. The light yield and its dependence on the integration time were measured and compared with that of the Bi4Ge3O12crystal. The total mass attenuation coefficient at 662 keV γ-rays was also determined and compared with the theoretical one calculated using the WinXCom program. ? 2016 Trans Tech Publications, Switzerland. |
会议录 | Applied Physics and Material Applications II
![]() |
语种 | 英语 |
内容类型 | 会议论文 |
源URL | [http://ir.siom.ac.cn/handle/181231/27435] ![]() |
专题 | 上海光学精密机械研究所_高功率激光单元技术研发中心 |
作者单位 | 中国科学院上海光学精密机械研究所 |
推荐引用方式 GB/T 7714 | Babin, Vladimir,Lertloypanyachai, Prapon,Pattanaboonmee, Nakarin,et al. Luminescence and scintillation response of Ce3+-doped oxide glasses with high Gd2O3content[C]. 见:. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论