Luminescence and scintillation of high silica glass containing SnO | |
Zheng, Shupei; Jiang, Xiaobo; Fan, Shaohua; Chen, Danping; Yang, Ke | |
刊名 | Mater. Lett.
![]() |
2017 | |
卷号 | 204页码:5 |
通讯作者 | dpchen2008@aliyun.com |
英文摘要 | High silica glasses containing SnO were prepared by sintering solution-doped porous silica glasses. The sample sintered in the CO reducing atmosphere exhibited a strong emission at 400 nm under 269 nm excitation with a lifetime of 11 mu s, and its intensity was much stronger compared to that of the sample sintered in the air atmosphere. Under X-ray excitation, broad radioluminescence ranging from 300 to 600 nm was observed and the maximum integral intensity was 122% of Bi4Ge3O12 (BGO). |
收录类别 | SCI |
资助信息 | National Natural Science Foundation of China [51272262, 61405215] |
WOS记录号 | WOS:000404709400002 |
内容类型 | 期刊论文 |
源URL | [http://ir.siom.ac.cn/handle/181231/28299] ![]() |
专题 | 上海光学精密机械研究所_高功率激光单元技术研发中心 |
作者单位 | 中国科学院上海光学精密机械研究所 |
推荐引用方式 GB/T 7714 | Zheng, Shupei,Jiang, Xiaobo,Fan, Shaohua,et al. Luminescence and scintillation of high silica glass containing SnO[J]. Mater. Lett.,2017,204:5. |
APA | Zheng, Shupei,Jiang, Xiaobo,Fan, Shaohua,Chen, Danping,&Yang, Ke.(2017).Luminescence and scintillation of high silica glass containing SnO.Mater. Lett.,204,5. |
MLA | Zheng, Shupei,et al."Luminescence and scintillation of high silica glass containing SnO".Mater. Lett. 204(2017):5. |