THE EFFECT OF RADIATION-INDUCED CROSS-LINKING ON THE RELAXATION OF TAUT TIE MOLECULES DURING ANNEALING OF DRAWN LDPE | |
YAN RJ ; LUO YX ; JIANG BZ | |
刊名 | journal of applied polymer science
![]() |
1993 | |
卷号 | 47期号:5页码:789-796 |
关键词 | POLYETHYLENE POLYPROPYLENE |
ISSN号 | 0021-8995 |
通讯作者 | yan rj |
中文摘要 | shrinkage, retractive stress, and infrared dichroism of the drawn low-density polyethylene (ldpe) as-drawn and irradiated by co-60-ray have been measured under different annealing conditions. the shrinkage and the disorientation of the irradiated sample was undergone more rapidly than that of unirradiated one as the temperature was continuously increased, surpassing a certain value, and a higher degree of shrinkage and disorientation was achieved finally for the irradiated sample when the samples were annealed with free ends. for the samples heated isothermally with fixed ends, the retractive stress went through a maximum and then attenuated to a limited value, and the degree of such a stress attenuation for the unirradiated sample was much more than that for the irradiated sample. these results show that the taut tie molecules (ttms) in drawn pe can relax by the pulling of chain segments out of crystal blocks that they anchored in at elevated temperatures higher than the a transition and also by the displacing of microfibrils if the samples were annealed with free ends. the cross-links produced by irradiation prohibit the former process. it was further observed that the dependence of the average extinction coefficient of the band at 2016 cm-1 on that of the band at 1894 cm-1 is related to irradiation and annealing conditions, which has also been explained by the relaxation of ttms and the function of irradiation-induced cross-linking on the relaxation. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
公开日期 | 2011-01-19 ; 2011-06-10 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/36309] ![]() |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | YAN RJ,LUO YX,JIANG BZ. THE EFFECT OF RADIATION-INDUCED CROSS-LINKING ON THE RELAXATION OF TAUT TIE MOLECULES DURING ANNEALING OF DRAWN LDPE[J]. journal of applied polymer science,1993,47(5):789-796. |
APA | YAN RJ,LUO YX,&JIANG BZ.(1993).THE EFFECT OF RADIATION-INDUCED CROSS-LINKING ON THE RELAXATION OF TAUT TIE MOLECULES DURING ANNEALING OF DRAWN LDPE.journal of applied polymer science,47(5),789-796. |
MLA | YAN RJ,et al."THE EFFECT OF RADIATION-INDUCED CROSS-LINKING ON THE RELAXATION OF TAUT TIE MOLECULES DURING ANNEALING OF DRAWN LDPE".journal of applied polymer science 47.5(1993):789-796. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论