MELTING BEHAVIOR OF DRAWN POLYPROPYLENE | |
YAN RJ ; JIANG BZ | |
刊名 | journal of polymer science part b-polymer physics |
1993 | |
卷号 | 31期号:9页码:1089-1094 |
关键词 | POLYETHYLENE POLYMERS FUSION |
ISSN号 | 0887-6266 |
通讯作者 | yan rj |
中文摘要 | the melting behavior of drawn, compression-molded isotactic polypropylene has been examined in terms of the influence of drawing conditions on the observed properties. two endothermic peaks were observed on differential scanning calorimetry (dsc) for samples when high draw ratios and high heating rates were used during dsc tests. the peak at lower temperature is influenced by draw ratio, temperature, and rate, and exhibits a strong superheating effect. the species associated with this peak can partially recrystallize into another species associated with the peak at higher temperature during dsc measurements. the position of the peak at higher temperature depends only on draw ratio. it is proposed that the double-melting peaks at lower and higher temperature result from extremely thin quasi-amorphous or crystalline layers between microfibrils and the lamellar crystals within microfibrils, respectively. (c) 1993 john wiley & sons, inc. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
公开日期 | 2011-01-19 ; 2011-06-10 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/36107] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | YAN RJ,JIANG BZ. MELTING BEHAVIOR OF DRAWN POLYPROPYLENE[J]. journal of polymer science part b-polymer physics,1993,31(9):1089-1094. |
APA | YAN RJ,&JIANG BZ.(1993).MELTING BEHAVIOR OF DRAWN POLYPROPYLENE.journal of polymer science part b-polymer physics,31(9),1089-1094. |
MLA | YAN RJ,et al."MELTING BEHAVIOR OF DRAWN POLYPROPYLENE".journal of polymer science part b-polymer physics 31.9(1993):1089-1094. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论