CURE AND IONIC-CONDUCTIVITY OF A 2-COMPONENT EPOXY NETWORK POLYMER ELECTROLYTE

	CURE AND IONIC-CONDUCTIVITY OF A 2-COMPONENT EPOXY NETWORK POLYMER ELECTROLYTE
	WU SY ; PENG XS ; SONG YX ; ZHOU ZN ; LIN YQ ; CHEN DL ; WANG FS
刊名	solid state ionics
	1995
卷号	76 期号:1-2 页码:163-172
关键词	LITHIUM PERCHLORATE MOBILITY
ISSN号	0167-2738
中文摘要	in order to raise the room temperature ionic conductivity and improve the mechanical strength of a peo-based polymer electrolyte, a non-crystalline two-component epoxy network was synthesized by curing diglycidyl ether of polyethylene glycol (dgepeg) with triglycidyl ether of glycerol (tgeg) in the presence of liclo4 salt, which acts in this system as both a ring opening catalyst and a source of ionic carrier. the structure of the precursors, the curing process and the cured films have been characterized by c-13 nmr, ir, dsc and ionic conductivity measurement techniques. the electrolyte system exhibits an ionic conductivity as high as similar to 10(-5) s/cm at 25 degrees c and is mechanically self-supportable. the dependence of ionic conductivity was investigated as a function of temperature, salt content, mw of peg segment in dgepeg and the proportion of dgepeg in dgepeg/tgeg ratio.
收录类别	SCI收录期刊论文
语种	英语
公开日期	2010-12-30 ; 2011-06-10
内容类型	期刊论文
源URL	[http://ir.ciac.jl.cn/handle/322003/26705]
专题	长春应用化学研究所_长春应用化学研究所知识产出_期刊论文
推荐引用方式 GB/T 7714	WU SY,PENG XS,SONG YX,et al. CURE AND IONIC-CONDUCTIVITY OF A 2-COMPONENT EPOXY NETWORK POLYMER ELECTROLYTE[J]. solid state ionics,1995,76(1-2):163-172.
APA	WU SY.,PENG XS.,SONG YX.,ZHOU ZN.,LIN YQ.,...&WANG FS.(1995).CURE AND IONIC-CONDUCTIVITY OF A 2-COMPONENT EPOXY NETWORK POLYMER ELECTROLYTE.solid state ionics,76(1-2),163-172.
MLA	WU SY,et al."CURE AND IONIC-CONDUCTIVITY OF A 2-COMPONENT EPOXY NETWORK POLYMER ELECTROLYTE".solid state ionics 76.1-2(1995):163-172.