Facile synthesis and photoluminescent properties of redispersible CeF3, CeF3 : Tb3+, and CeF3 : Tb3+/LaF3 (core/shell) nanoparticles | |
Wang ZL ; Quan ZW ; Jia PY ; Lin CK ; Luo Y ; Chen Y ; Fang J ; Zhou W ; O'Connor CJ ; Lin J | |
刊名 | chemistry of materials
![]() |
2006 | |
卷号 | 18期号:8页码:2030-2037 |
关键词 | POLYOL-MEDIATED SYNTHESIS NANOSCALE FUNCTIONAL MATERIALS DOPED LAF3 NANOPARTICLES CORE-SHELL NANOCRYSTALS UP-CONVERSION EMISSION LIQUID-PHASE SYNTHESIS ENERGY-TRANSFER EPITAXIAL-GROWTH QUANTUM DOTS THIN-FILMS |
ISSN号 | 0897-4756 |
通讯作者 | lin j |
中文摘要 | cef3, cef3:tb3+, and cef3:tb3+/laf3 (core/shell) nanoparticles were prepared by the polyol method and characterized by x-ray diffraction (xrd), transmission electron microscopy (tem), x-ray photoelectron spectra (xps), uv-vis absorption spectra, photoluminescence (pl) spectra, and lifetimes. the results of xrd indicate that the obtained cef3, cef3:tb3+, and cef3:tb3+/laf3 (core/shell) nanoparticles crystallized well at 200 degrees c in diethylene glycol (deg) with a hexagonal structure. the tem images illustrate that the cef3 and cef3:tb3+ nanoparticles are spherical with a mean diameter of 7 nm. the growth of the laf3 shell around the cef3:tb3+ core nanoparticles resulted in an increase of the average size (11 nm) of the nanopaticles as well as in a broadening of their size distribution. these nanocrystals can be well-dispersed in ethanol to form clear colloidal solutions. the colloidal solutions of cef3 and cef3:tb3+ show the characteristic emission of ce3+ 5d-4f (320 nm) and tb3+ d-5(4)-f-7(j) (j = 6-3, with d-5(4)-f-7(5) green emission at 542 nm as the strongest one) transitions, respectively. the emission intensity and lifetime of the cef3:tb3+/laf3 (core/shell) nanoparticles increased with respect to those of cef3:tb3+ core particles. |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000236961600006 |
公开日期 | 2010-08-17 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/15891] ![]() |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Wang ZL,Quan ZW,Jia PY,et al. Facile synthesis and photoluminescent properties of redispersible CeF3, CeF3 : Tb3+, and CeF3 : Tb3+/LaF3 (core/shell) nanoparticles[J]. chemistry of materials,2006,18(8):2030-2037. |
APA | Wang ZL.,Quan ZW.,Jia PY.,Lin CK.,Luo Y.,...&Lin J.(2006).Facile synthesis and photoluminescent properties of redispersible CeF3, CeF3 : Tb3+, and CeF3 : Tb3+/LaF3 (core/shell) nanoparticles.chemistry of materials,18(8),2030-2037. |
MLA | Wang ZL,et al."Facile synthesis and photoluminescent properties of redispersible CeF3, CeF3 : Tb3+, and CeF3 : Tb3+/LaF3 (core/shell) nanoparticles".chemistry of materials 18.8(2006):2030-2037. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论