Preparation and properties of microporous membrane from poly(vinylidene fluoride-co-tetrafluoroethylene) (F2.4) for membrane distillation | |
Feng CS ; Shi BL ; Li GM ; Wu YL | |
刊名 | journal of membrane science |
2004 | |
卷号 | 237期号:1-2页码:15-24 |
关键词 | ADHESION |
ISSN号 | 0376-7388 |
通讯作者 | wu yl |
中文摘要 | flat-sheet microporous membranes from f2.4 for membrane distillation (md) were prepared by phase inversion process. dimethylacetamide (dmac) and liclo(4)(.)3h(2)o/trimethyl phosphate (tmp) were, respectively, used as solvent and pore-forming additives. the effects of casting solution composition, exposure time prior to coagulation and temperature of precipitation bath on f2.4 membrane structure were investigated. the morphology of resultant porous membrane was observed by scanning electron microcopy. some natures of f2.4 porous membrane after drying in air, such as mechanical properties and hydrophobicity, were exhibited and compared with poly(vinylidene fluoride) (pvdf) membrane prepared by the same ways. stress-at-break and strength stress of f2.4 microporous membrane are higher than that of pvdf membrane, and elongation percentage of f2.4 membrane at break is about eight-fold as great as that of pvdf membrane. contact angle of f2.4 microporous membrane to water (86.6 +/- 0.51degrees) was also larger than that of pvdf mernbrane (80.0 +/- 0.78degrees). md experiment was carried out using a direct contact membrane distillation (dcmd) configuration as final test to permeate performance of resultant microporous membrane. |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000221920500003 |
公开日期 | 2010-08-17 |
内容类型 | 期刊论文 |
源URL | [http://202.98.16.49/handle/322003/15823] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Feng CS,Shi BL,Li GM,et al. Preparation and properties of microporous membrane from poly(vinylidene fluoride-co-tetrafluoroethylene) (F2.4) for membrane distillation[J]. journal of membrane science,2004,237(1-2):15-24. |
APA | Feng CS,Shi BL,Li GM,&Wu YL.(2004).Preparation and properties of microporous membrane from poly(vinylidene fluoride-co-tetrafluoroethylene) (F2.4) for membrane distillation.journal of membrane science,237(1-2),15-24. |
MLA | Feng CS,et al."Preparation and properties of microporous membrane from poly(vinylidene fluoride-co-tetrafluoroethylene) (F2.4) for membrane distillation".journal of membrane science 237.1-2(2004):15-24. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论