	图形化Si基Ge薄膜热应变的有限元分析; Thermal Strain Finite-element Analysis in Ge Film on Patterned Si Substrate
	高玮 ; 亓东锋 ; 韩响 ; 陈松岩 ; 李成 ; 赖虹凯 ; 黄巍 ; 李俊
	2014-09-28
关键词	图形化衬底 Ge/Si 有限元法 热失配 应变 patterned substrate Ge/Si finite element thermal mismatch strain
英文摘要	利用有限元方法模拟了图形化SI衬底上外延gE薄膜的热失配应变,研究了薄膜内部以及表面的应变分布情况,分析了应变与薄膜厚度、衬底尺寸的变化关系.结果表明,热失配应变在异质结构的界面处最大,沿外延层生长方向递减;在薄膜表面,中心区域应变最大,由中心到边缘逐渐减小,边缘发生突变,急剧减小;不同的膜厚下,薄膜表面应变分布规律相同,并且薄膜越厚,应变越小;图形衬底单元的尺寸对薄膜应变有较大的影响,当衬底厚度在6μM以内,宽度在10μM以内时,更有利于薄膜应变的释放.; Film/substrate heterostructure based on patterned substrate has advantages in strain release and dislocation capture,and is widely used in microelectronics and optoelectronics.Residual stress in heterostructure leads to negative effects on the performance of the material and devices.Finite element method is used in this paper to simulate thermal mismatch strain in epitaxial film on patterned Si substrate.Strain distribution is analyzed which is from the inside out of the film and the strain against film thickness and substrate size are obtained.The results indicate that maximal thermal mismatch appears in the interface of film/substrate heterostructure,and the thermal mismatch is smaller from the interface to the epitaxial film surface;strain decreases gradually from center to edge and suddenly drops on the edge;strain distribution of the film is in the same rule with different thickness and thin film means small strain;size of the substrate has great influence on film strain,strain release of the epitaxial film can be accepted when the substrate thickness and width are 6μm and 10μm respectively.; 国家重点基础研究发展计划(973)项目(2012CB933503;2013CB632103); 国家自然科学基金(61176050;61036003;61176092); 福建省政府项目(2012H0038); 中央高校基本科研业务经费(2010121056)
语种	zh_CN
内容类型	期刊论文
源URL	[http://dspace.xmu.edu.cn/handle/2288/105837]
专题	航空航天－已发表论文
推荐引用方式 GB/T 7714	高玮,亓东锋,韩响,等. 图形化Si基Ge薄膜热应变的有限元分析, Thermal Strain Finite-element Analysis in Ge Film on Patterned Si Substrate[J],2014.
APA	高玮.,亓东锋.,韩响.,陈松岩.,李成.,...&李俊.(2014).图形化Si基Ge薄膜热应变的有限元分析..
MLA	高玮,et al."图形化Si基Ge薄膜热应变的有限元分析".(2014).