介孔NiO制备及其在超级电容器的应用; Synthesis of Mesoporous Nickel Oxide for Supercapacitor Application | |
陈璇璇 ; 赵真真 ; 王登超 ; 黄中杰 ; 倪文彬 ; 余力 ; 赵健伟 ; CHEN Xuan-xuan ; ZHAO Zhen-zhen ; WANG Deng-chao ; HUANG Zhong-jie ; NI Wen-bin ; YU Li ; ZHAO Jian-wei | |
刊名 | http://electrochem.xmu.edu.cn/CN/abstract/abstract8361.shtml
![]() |
2011-02-28 | |
关键词 | 超级电容器 介孔氧化镍 稳定性 supercapacitor mesoporous nickel oxide cycle-life stability |
英文摘要 | 应用金属有机配合物作前驱体,煅烧制备有稳定结构的介孔NiO电极.TEM孔径分布及电化学测试表明,该电极结构规整,平均孔径为30 nm.在2.0 A·g-1电流密度下,比电容为72 F·g-1.1000次循环后,几乎无衰减,而且其表面介孔结构相当稳定.; Mesoporous nickel oxide has been synthesized by calcining metal-organic coordination precursor.Transmission electron microscopy and BET test showed that the prepared NiO had a regular morphology and displayed a narrow size distribution.Electrochemical tests revealed that such mesoporous NiO had a specific capacity of 72 F·g-1 at the current of 2.0 A·g-1.Futhermore,the material showed excellent cycle-life stability.There was no degradation of capacitance after 1000 cycles.; 作者联系地址:南京大学化学化工学院生命分析教育部重点实验室;; Author's Address: School of Chemistry and Chemical Engineering,Key Laboratory of Analytical Chemistry for Life ScienceMOE,Nanjing University,Nanjing 210008,China |
语种 | 中文 |
出版者 | 厦门大学《电化学》编辑部 |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/58387] ![]() |
专题 | 2011年第17卷 |
推荐引用方式 GB/T 7714 | 陈璇璇,赵真真,王登超,等. 介孔NiO制备及其在超级电容器的应用, Synthesis of Mesoporous Nickel Oxide for Supercapacitor Application[J]. http://electrochem.xmu.edu.cn/CN/abstract/abstract8361.shtml,2011. |
APA | 陈璇璇.,赵真真.,王登超.,黄中杰.,倪文彬.,...&ZHAO Jian-wei.(2011).介孔NiO制备及其在超级电容器的应用.http://electrochem.xmu.edu.cn/CN/abstract/abstract8361.shtml. |
MLA | 陈璇璇,et al."介孔NiO制备及其在超级电容器的应用".http://electrochem.xmu.edu.cn/CN/abstract/abstract8361.shtml (2011). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论