MnO_2/聚苯胺复合材料的电化学电容; Electrochemical Capacitance of MnO_2 /PANI Composite | |
徐小存 ; 刘开宇 ; 殷志刚 ; 孙哲 ; 苏耿 ; XU Xiao-cun ; LIU Kai-yu ; YIN Zhi-gang ; SUN Zhe ; SU Geng | |
刊名 | http://electrochem.xmu.edu.cn/CN/abstract/abstract8460.shtml
![]() |
2010-02-28 | |
关键词 | MnO2 聚苯胺 复合材料 超级电容器 电化学性能 软模板 MnO2 polyaniline composites supercapacitor electrochemical property soft-template |
英文摘要 | 以P123为模板剂,软模板法制备出纳米MnO2.酸性条件下引入苯胺并聚合,得到了MnO2/聚苯胺复合材料.X射线衍射(XRD)、红外光谱(IR),扫描电子显微镜(SEM)表征观察样品的结构、形貌.循环伏安、交流阻抗、恒电流充放电等测试MnO2/聚苯胺电极的电化学性能.结果表明:引入苯胺改变了样品纳米MnO2的形貌.MnO2/聚苯胺电极比容量高达190.8F·g-1,500次循环电极比容量仅衰减4.7%,库仑效率均保持在97%以上.; Nano-MnO2 was prepared by using P123 as a soft template.The MnO2 /polyaniline composite was further prepared by polymerization of aniline with the nano-MnO2 in acidic conditions and was investigated by XRD and IR.The morphology of nano-MnO2 observed by SEM was changed with the introduction of aniline.The electrochemical properties of MnO2 /PANI electrode were investigated using cyclic voltammetry,galvanostatic charge-discharge and electrochemical impedance spectroscopy.The specific capacitance of MnO2 /PANI electrode could reach as high as 190.8 F·g-1,which decayed only 4.7% over 500 cycles.And the coulombic efficiency has been maintained at above 97%.; 作者联系地址:中南大学化学化工学院;; Author's Address: College of Chemistry and Chemical engineering,Central South University,Changsha 410083,Hunan,China |
语种 | 中文 |
出版者 | 厦门大学《电化学》编辑部 |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/58374] ![]() |
专题 | 2010年第16卷 |
推荐引用方式 GB/T 7714 | 徐小存,刘开宇,殷志刚,等. MnO_2/聚苯胺复合材料的电化学电容, Electrochemical Capacitance of MnO_2 /PANI Composite[J]. http://electrochem.xmu.edu.cn/CN/abstract/abstract8460.shtml,2010. |
APA | 徐小存.,刘开宇.,殷志刚.,孙哲.,苏耿.,...&SU Geng.(2010).MnO_2/聚苯胺复合材料的电化学电容.http://electrochem.xmu.edu.cn/CN/abstract/abstract8460.shtml. |
MLA | 徐小存,et al."MnO_2/聚苯胺复合材料的电化学电容".http://electrochem.xmu.edu.cn/CN/abstract/abstract8460.shtml (2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论