中温NaCl-水蒸气协同作用下铁的腐蚀机理; The Mechanism of Electrochemical Testing Method under Synergistic Effect of NaCl and Water Vapor at 600℃ | |
刘莉 ; 李瑛 ; 王福会 ; LIU Li ; LI Ying ; WANG Fu-hui | |
刊名 | http://electrochem.xmu.edu.cn/CN/abstract/abstract8523.shtml
![]() |
2009-05-28 | |
关键词 | 水蒸气 固态NaCl 交流阻抗 氧化 water vapor synergistic effect EIS oxidation |
英文摘要 | 应用电偶电流测试法研究在中温固态NaCl盐膜-水蒸气协同作用下,纯铁的腐蚀电化学反应机理.交流阻抗(EIS)法和SEM测试表明,阻抗谱能有效地表征材料表面氧化膜的存在以及反应过程氧化物的变化趋势,其中金属的氧化层电阻与腐蚀速率之间有较好的对应关系.; The existence of electrochemical reaction during the corrosion process of pure Fe under a deposit of solid NaCl in water vapor at above 400 ℃ had been detected by measuring the corrosion current using double-layer electrode.In EIS measurement,only one capacitive loop was obtained on the pure metals and this gave the information of oxide layer on them.The electrochemical impedance spectroscopy(EIS) and scanning-electron microscopy(SEM) results testified that there is a good relationship between the resistance of oxide layer Rox and the corresion reaction rate for pure metals with different oxidation times.The electrochemical technique is an effective method for studying corrosion performance at high temperature.; 作者联系地址:中国科学院金属研究所金属腐蚀与防护国家重点实验室;; Author's Address: State Key Laboratory for Corrosion and Protection,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China |
语种 | 中文 |
出版者 | 厦门大学《电化学》编辑部 |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/58261] ![]() |
专题 | 2009年第15卷 |
推荐引用方式 GB/T 7714 | 刘莉,李瑛,王福会,等. 中温NaCl-水蒸气协同作用下铁的腐蚀机理, The Mechanism of Electrochemical Testing Method under Synergistic Effect of NaCl and Water Vapor at 600℃[J]. http://electrochem.xmu.edu.cn/CN/abstract/abstract8523.shtml,2009. |
APA | 刘莉,李瑛,王福会,LIU Li,LI Ying,&WANG Fu-hui.(2009).中温NaCl-水蒸气协同作用下铁的腐蚀机理.http://electrochem.xmu.edu.cn/CN/abstract/abstract8523.shtml. |
MLA | 刘莉,et al."中温NaCl-水蒸气协同作用下铁的腐蚀机理".http://electrochem.xmu.edu.cn/CN/abstract/abstract8523.shtml (2009). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论