	纳米Na_2SiF_6的电化学制备、表征与荧光性质; Electrochemical Synthesis,Characterization and Fluorescence Property of nano Na_2SiF_6
	秦国旭 ; 万新军 ; 袁希梅 ; 褚道葆 ; QIN Guo-xu ; WAN Xin-jun ; YUAN Xi-mei ; CHU Dao-bao
刊名	http://electrochem.xmu.edu.cn/CN/abstract/abstract8608.shtml
	2008-08-28
关键词	Na2SiF6纳米粒子多孔nanoTiO2电极电化学沉积表征荧光性质 nanoparticle of Na2SiF6 nanoporous TiO2 film electrode electrochemical deposition characterization fluorescence property
英文摘要	采用溶胶-凝胶法在Ti表面修饰一层纳米TiO2(nanoTiO2)膜,经X射线粉末衍射(XRD)和扫描电镜(SEM)表征,证明多孔TiO2膜的平均孔径为80 nm.以该多孔膜电极为模板,借助电化学沉积的方法制备了纳米Na2SiF6(nano Na2SiF6).经XRD和透射电镜(TEM)测试证实该Na2SiF6为均一的白锰钒型结构,平均粒径约为20 nm.初步研究了其荧光性质,发现在452.4 nm和285 nm处分别有强的荧光发射峰和激发峰.; The nano TiO2 film was prepared by sol-gel process and characterized with X-ray diffraction(XRD) and scanning electron microscope(SEM).It was found that the average size of pore diameter was about 80 nm for the nano TiO2 film.The Nano Na2SiF6 was synthesized by electrochemical deposition on the nanoporous film electrode and characterized with XRD and transmission electron microscope(TEM).The result showed that the average size of nanoparticle was 20 nm for the nano Na2SiF6.The fluorescence property of nano Na2SiF6 was also studied briefly.The result indicated that the nano Na2SiF6 exhibited strong fluorescence emission at 452.4 nm and 285 nm,respectively.; 作者联系地址：巢湖学院化学系新型内能材料与精细化学品研究所;安徽恒锐新技术开发有限责任公司;安徽师范大学化学与材料科学学院;; Author's Address: 1.Department of Chemistry,Laboratory of Novel Functional Material and Fine Chemicals,Chaohu NormalCollege,Chaohu 238000,Anhui,China;2.College of Chemistry and Materials Science,Anhui Normal University,Wuhu 241000,Anhui,China;3.Anhui Horae New TechnologyDevelopment Co.,Ltd,Hefei 230088,Anhui,China
语种	中文
出版者	厦门大学《电化学》编辑部
内容类型	期刊论文
源URL	[http://dspace.xmu.edu.cn/handle/2288/58158]
专题	2008年第14卷
推荐引用方式 GB/T 7714	秦国旭,万新军,袁希梅,等. 纳米Na_2SiF_6的电化学制备、表征与荧光性质, Electrochemical Synthesis,Characterization and Fluorescence Property of nano Na_2SiF_6[J]. http://electrochem.xmu.edu.cn/CN/abstract/abstract8608.shtml,2008.
APA	秦国旭.,万新军.,袁希梅.,褚道葆.,QIN Guo-xu.,...&CHU Dao-bao.(2008).纳米Na_2SiF_6的电化学制备、表征与荧光性质.http://electrochem.xmu.edu.cn/CN/abstract/abstract8608.shtml.
MLA	秦国旭,et al."纳米Na_2SiF_6的电化学制备、表征与荧光性质".http://electrochem.xmu.edu.cn/CN/abstract/abstract8608.shtml (2008).