MnO_2/C复合材料的电化学电容特性研究

CORC > 厦门大学 > 2007年第13卷

	MnO_2/C复合材料的电化学电容特性研究; Electrochemical Capacitance Characteristics for MnO_2/C Composite
	高军 ; 黄行康 ; 杨勇 ; GAO Jun ; HUANG Xing-kang ; YANG Yong
刊名	http://electrochem.xmu.edu.cn/CN/abstract/abstract8713.shtml
	2007-08-28
关键词	电化学电容 MnO2/C复合材料比电容 electrochemical capacitor MnO2/C composite specific capacitance
英文摘要	应用乙炔黑直接还原高锰酸钾制备MnO2/C复合材料.样品结构及性能由XRD和SEM表征.研究了MnO2/C电极(正极)在不同电解液中的法拉第"准电容行为",及其循环伏安、交流阻抗与恒电流充放电等性能.实验表明,MnO2/C复合材料具有良好的电化学电容特性.在1 mol/L的KOH电解液中和电流密度为5 mA/cm2下,MnO2/C复合材料的比电容量可达258 F/g,并表现出良好的循环性能.; The MnO2/C composite was synthesized by reduction of KMnO4 with acetylene black.The products were characterized by XRD and SEM.We used MnO2/C composite as the positive electrode material of the electrochemical capacitor.The performance of faradic psedocapacitance of the MnO2/C electrode was studied in different electrolytes.The MnO2/C electrode was tested by cyclic voltammetry,electrochemical impedance spectroscopy(EIS) and constant charge-discharge curves.The experimental results showed that the MnO2/C composite has excellent performance.The specific capacitance of the MnO2/C composite as 258 F/g is obtained at 5mA/cm2 current density in 1mol/L KOH solution.It exhibited high discharge capacity and good cycle performance.; 作者联系地址：厦门大学化学系,厦门大学化学系,厦门大学化学系福建厦门361005,福建厦门361005,福建厦门361005; Author's Address: Department of Chemistry,Xiamen University,Xiamen 361005,Fujian,China
语种	中文
出版者	厦门大学《电化学》编辑部
内容类型	期刊论文
源URL	[http://dspace.xmu.edu.cn/handle/2288/58071]
专题	2007年第13卷
推荐引用方式 GB/T 7714	高军,黄行康,杨勇,等. MnO_2/C复合材料的电化学电容特性研究, Electrochemical Capacitance Characteristics for MnO_2/C Composite[J]. http://electrochem.xmu.edu.cn/CN/abstract/abstract8713.shtml,2007.
APA	高军,黄行康,杨勇,GAO Jun,HUANG Xing-kang,&YANG Yong.(2007).MnO_2/C复合材料的电化学电容特性研究.http://electrochem.xmu.edu.cn/CN/abstract/abstract8713.shtml.
MLA	高军,et al."MnO_2/C复合材料的电化学电容特性研究".http://electrochem.xmu.edu.cn/CN/abstract/abstract8713.shtml (2007).