表面覆CoOOH的球形Ni(OH)_2的制备及快充性能; Preparation of Spherical Ni(OH)_2 Coated with CoOOH and Its Fast Charge Performance | |
杨敏杰 ; 南俊民 ; 侯宪鲁 ; 薛建军 ; 崔燕 ; 崔明 ; YANG Min-jie | |
刊名 | http://electrochem.xmu.edu.cn/CN/abstract/abstract8846.shtml
![]() |
2006-05-28 | |
关键词 | 球形Ni(OH)2 表面包覆 CoOOH 快速充电 Spherical nickel hydroxide Surface modification CoOOH Fast charge |
英文摘要 | 应用化学沉淀-电化学氧化法,于球形N i(OH)2颗粒表面生成CoOOH包覆层,研究包覆处理对AA型高容MH/N i电池快充性能的影响,并由红外光谱和扫描电镜表征覆钴样品.结果表明,以包覆CoOOH的N i(OH)2作正极活性材料装配的电池较之于正极单一添加CoO的电池,其内阻降低了约3.4 mΩ,该电池快充时充电电压平台较低且在充电末期电池温度不超过55℃,首次放电效率达90.6%,快充循环寿命达300周次.; Spherical Ni(OH)_(2) was coated with CoOOH through chemical precipitation and electrolytic oxidation.The influences of CoOOH coating on fast charge performance ofMH/Ni battery were studied by preparing high capacity and fast charge AA size MH/Ni batteries.The sample coated with CoOOH was characterized by Infrared spectrum(IR) and scanning electron microscopy(SEM).The results showed that the internal resistance decreased 3.4 mΩ,the charge plateau lower and the cell temperrature was below 55 ℃ at the end of charging process when the cathode active material used Ni(OH)_2 coated with CoOOH as compared with that doped by CoO.In addition,an initial discharge efficiency of 90.6% and over 300 cycles lifetime were achieved when the batteries were fast charged.; 作者联系地址:华南师范大学化学与环境学院,华南师范大学化学与环境学院,广州市鹏辉电池有限公司,广州市鹏辉电池有限公司,天津大学化工学院,华南师范大学化学与环境学院 广东广州510006,广东广州510006,广东广州511483,广东广州511483,天津300072,广东广州510006; Author's Address: 1,NAN Jun-min~*1,HOU Xian-lu~2,XUE Jian-jun~2,CUI Yan~3,CUI Ming~11.School of Chemistry and Environment,South China Normal University,Guangzhou,51006,Guangdong,China,2.Guangzhou Great Power Battery Co.,Ltd,Guangzhou 511483,Guangdong,China,3.School of Chemical Engineering and Technology,Tianjin University,Tianjin 30072,China |
语种 | 中文 |
出版者 | 厦门大学《电化学》编辑部 |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/58013] ![]() |
专题 | 2006年第12卷 |
推荐引用方式 GB/T 7714 | 杨敏杰,南俊民,侯宪鲁,等. 表面覆CoOOH的球形Ni(OH)_2的制备及快充性能, Preparation of Spherical Ni(OH)_2 Coated with CoOOH and Its Fast Charge Performance[J]. http://electrochem.xmu.edu.cn/CN/abstract/abstract8846.shtml,2006. |
APA | 杨敏杰.,南俊民.,侯宪鲁.,薛建军.,崔燕.,...&YANG Min-jie.(2006).表面覆CoOOH的球形Ni(OH)_2的制备及快充性能.http://electrochem.xmu.edu.cn/CN/abstract/abstract8846.shtml. |
MLA | 杨敏杰,et al."表面覆CoOOH的球形Ni(OH)_2的制备及快充性能".http://electrochem.xmu.edu.cn/CN/abstract/abstract8846.shtml (2006). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论