某些离子对Cr_2O_7~（2－）阳极形成过程的影响

CORC > 厦门大学 > 1995年第1卷

	某些离子对Cr_2O_7~（2－）阳极形成过程的影响; The EHect of Some Ions on Anodic Formation Process at Pt and PbO_2 Electrodes
	金世雄 ; 周志刚 ; 王岚 ; Jin Shixiong ; Zhou Zhigang ; Wang Lan
刊名	http://electrochem.xmu.edu.cn/CN/abstract/abstract9769.shtml
	1995-02-28
关键词	Platinum electrode Lead dioxide electrode Anodic formation of Cr_2O ion Anodic evolution of oxygen
英文摘要	某些离子对Ｃｒ_２Ｏ_７~（２－）阳极形成过程的影响金世雄，周志刚，王岚（南开大学化学系，天津３０００７１）Ｃｒ（Ⅲ）阳极氧化为Ｃｒ（Ⅵ）是工业制取铬酸及其盐类的主要方法，也是从含铬工业废水中回收Ｃｒ（Ⅵ）的主要途径．文献￣［１］曾表明，Ｃｒ（Ⅲ）的阳?..; The influence of Ag_2SO_4,Li_2SO_4,Na_2SO_4,K_2SO_4,NH_4)_2SO_4,MgSO_4 and KF onthe evolution of O_2 and the formation of Cr_2O at Pt and PbO_2 anodes was investigated in mixedH_2SO_4-Cr_2(SO_2)_3 solutions.The kinetic data related respectively to Cr_2O formation and O_2 evolutionat Pt and PbO_2 anodes were measured by method of resolving the steady-state polarization curve.TheTafel slope of steady-state ～1g i relationships for Cr_2O formation reaction is close to 2×2. 303RT/βF,whereas for O_2 evolution it is close to 2.303 RT/βF(with β=0.5). The results indicate thatthe current efficiency for Cr_2O formation is increased by adding Ag￣+ ions to the anolyte and decreasedby adding Li￣+,Na￣+,K￣+,NH and Mg￣(2+) ions to the anolyte at Pt electrode.While on PbO_2 electrode,the current efficiency of Cr_2O formation is decreased by adding Ag￣+ and F￣- ions to the anolyte andincreased by adding K￣+ ions to the anolyte.; 作者联系地址：南开大学化学系; Author's Address: Department of Chemistry,Nankai University,Tianjin 300071
语种	中文
出版者	厦门大学《电化学》编辑部
内容类型	期刊论文
源URL	[http://dspace.xmu.edu.cn/handle/2288/57194]
专题	1995年第1卷
推荐引用方式 GB/T 7714	金世雄,周志刚,王岚,等. 某些离子对Cr_2O_7~（2－）阳极形成过程的影响, The EHect of Some Ions on Anodic Formation Process at Pt and PbO_2 Electrodes[J]. http://electrochem.xmu.edu.cn/CN/abstract/abstract9769.shtml,1995.
APA	金世雄,周志刚,王岚,Jin Shixiong,Zhou Zhigang,&Wang Lan.(1995).某些离子对Cr_2O_7~（2－）阳极形成过程的影响.http://electrochem.xmu.edu.cn/CN/abstract/abstract9769.shtml.
MLA	金世雄,et al."某些离子对Cr_2O_7~（2－）阳极形成过程的影响".http://electrochem.xmu.edu.cn/CN/abstract/abstract9769.shtml (1995).