| 题名 | 用于白光LED的近紫外激发硼酸盐荧光粉的研制; The research and preparation of Borate phosphor by near ultraviolet excited for white-light LED |
| 作者 | 王荣 |
| 答辩日期 | 2012 ; 2012 |
| 导师 | 徐进 |
| 关键词 | 高温固相法 Sr3B2O6：Eu3+荧光粉 Sr2B2O5: Tb3+, Li+ 荧光粉 Solid-state reaction method Sr3B2O6: Eu3+ phosphors Sr2B2O5: Tb3+, Li+ phosphors |
| 英文摘要 | 目前商业化的白光LED主要是采用GaN基蓝光LED芯片与YAG：Ce3+黄色荧光粉组合，利用蓝光芯片激发YAG荧光粉产生的黄光与剩余蓝光混合获得白光。但此种方式得到的白光不够均匀、色温较高、显色指数较低，不适合于室内照明。为了克服这些缺点，本文采用近紫外LED芯片来激发红绿蓝（RGB）三基色荧光粉而实现低色温、高显色指数的白光，希望能应用于室内照明。稀土掺杂硼酸盐类发光材料因具有很高的紫外透明性、非线性特性、良好的稳定性及光学性能等特性，故有望成为一种极具潜力的三基色荧光材料。文主要研究了Sr3B2O6：Eu3+，Na+红色荧光粉、Sr2B2O5:Tb3+，Li+绿蓝色荧光粉和Sr2B2O5:...; The currently commercial WLEDs are obtained mainly by combining a 460 nm blue-emitting GaN chip with a yellow-emitting yttrium aluminum garnet (YAG) doped Ce3+ phosphor. However, the thermal quenching characteristic of commonly used YAG: Ce3+ phosphor is still not satisfactory and the corresponding white LEDs encounter some problems, such as low color-rendering index, low color reproducibility and...; 学位：工学硕士; 院系专业：材料学院材料科学与工程系_材料学; 学号：20720091150050 |
| 语种 | zh_CN |
| 出处 | http://210.34.4.13:8080/lunwen/detail.asp?serial=33741 |
| 内容类型 | 学位论文 |
| 源URL | [http://dspace.xmu.edu.cn/handle/2288/21889]  |
| 专题 | 材料学院－学位论文 |
| 推荐引用方式 GB/T 7714 | 王荣. 用于白光LED的近紫外激发硼酸盐荧光粉的研制, The research and preparation of Borate phosphor by near ultraviolet excited for white-light LED[D]. 2012, 2012. |