题名 | 低温水热一步法制备Ag/TiO2、W/TiO2 和(Ag, W)/TiO2及其表征; Preparation of Ag/TiO2, W/TiO2 and (Ag, W)/TiO2 by a One-Step Low-Temperature Hydrothermal Method and their Characterizations |
作者 | 王笛 |
答辩日期 | 2012 ; 2012 |
导师 | 周忠华 |
关键词 | TiO2 低温水热一步法 结晶Ag负载 W 掺杂 光催化 TiO2 one-step low-temperature hydrothermal method crystalline Ag-loaded W-doped photocatalytic activity |
英文摘要 | 近十年,TiO2光催化材料因其安全性、稳定性、高效性和低成本,在降解环境污染物领域受到广泛关注。但锐钛矿TiO2仍存在光子利用率低、光生电子空穴对复合迅速等缺点有待改善。 锐钛矿TiO2表面负载贵金属,能形成Schottky势垒;作为电子捕获剂有效阻止光生电子空穴对的复合。过渡金属掺杂可改变TiO2的晶体结构和禁带宽度,影响光谱响应范围。本文以提高TiO2光催化活性,制备同时对液相和气相有良好适应性的光催化剂为目的,以钛酸正丁酯和金属盐为原料,在水溶液中,用低温水热一步法,制备了结晶态纳米Ag负载、W掺杂和Ag/W双元素负载/掺杂的锐钛矿TiO2纳米颗粒。通过扫描电镜、透射电镜、X射线衍射、...; In recent decades, TiO2 photocatalytic materials have been of more and more interests in degradation of environmental pollutants due to their nontoxicity, stability, efficiency and low cost. However, anatase TiO2 has a limitation of photo-quantum efficiency and fast recombination of photogenerated electron-hole pairs, which are expected to be improved. Loading noble metal on the surface of TiO2 c...; 学位:工学硕士; 院系专业:材料学院材料科学与工程系_材料学; 学号:20720091150048 |
语种 | zh_CN |
出处 | http://210.34.4.13:8080/lunwen/detail.asp?serial=34509 |
内容类型 | 学位论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/21887] ![]() |
专题 | 材料学院-学位论文 |
推荐引用方式 GB/T 7714 | 王笛. 低温水热一步法制备Ag/TiO2、W/TiO2 和(Ag, W)/TiO2及其表征, Preparation of Ag/TiO2, W/TiO2 and (Ag, W)/TiO2 by a One-Step Low-Temperature Hydrothermal Method and their Characterizations[D]. 2012, 2012. |