题名 | 先驱体转化法制备含硼/铝碳化硅纤维的研究; Silicon Carbide Fibers Derived from Polycarbosilanes Containing Boron and Aluminium |
作者 | Xu M(许慜) |
答辩日期 | 2011 ; 2011 |
导师 | 陈立富 |
关键词 | 溶胶 烧结助剂 聚碳硅烷 碳化硅纤维 Colloid Sintering additives Polycarbosilane Silicon carbide fibers |
英文摘要 | 本研究较为系统地研究了以含铝和硼的聚碳硅烷为原料制备近化学计量比SiC纤维中的基础科学问题。 本论文发明了高稳定、高分散硼溶胶的制备技术。利用二甲基胺硼烷(DMAB)和低分子量聚碳硅烷(LPCS)在二甲苯(xylene)中的反应,控制反应条件:投料比为DMAB/LPCS/xylene=1/3/80(质量比),反应温度为350℃,反应时间为10h,可以获得高度稳定的硼溶胶。研究发现:硼溶胶的形成过程实质是LPCS中Si-H和DMAB中B-H的相互作用,使LPCS与DMAB发生脱氢反应,从而实现LPCS的化学交联。 将硼溶胶和纺丝级高分子量聚碳硅烷(HPCS)或含铝聚碳硅烷(PACS)共混,得...; A novel route for the synthesis of highly dispersed and highly stable boron-containing colloid has been invented in this work. Dimethylamine borane (DMAB) and low-molecular weight polycarbosilane (LPCS) were dissolved into xylene with the mass ratio of DMAB/LPCS/xylene =1/3/80. The resultant clear solution was heated to 350℃ and retained for 10h. After heating, a yellow colloid was formed. It has ...; 学位:工学硕士; 院系专业:材料学院材料科学与工程系_材料学; 学号:20720081150609 |
语种 | zh_CN |
出处 | http://210.34.4.13:8080/lunwen/detail.asp?serial=30532 |
内容类型 | 学位论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/21919] ![]() |
专题 | 材料学院-学位论文 |
推荐引用方式 GB/T 7714 | 许慜. 先驱体转化法制备含硼/铝碳化硅纤维的研究, Silicon Carbide Fibers Derived from Polycarbosilanes Containing Boron and Aluminium[D]. 2011, 2011. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论