Preparation and structure of porous carbons by pyrolysis of phenol formaldehyde resin | |
Lin L(林鹭) | |
2008 | |
关键词 | phenol formaldehyde resin conducting polymer foaming agent zinc chloride porous carbonaceous material |
英文摘要 | Soluble phenolic resin was synthesized by phenol and formaldehyde with NH(4)OH catalyst. Porous polyacenic semiconductor carbon (PPAS) materials were prepared by heat treatment of phenol formaldehyde (PF) resin doped with different contents of a foaming agent (ZnCl(2)) at lower temperatures (500 similar to 900 degrees C) in inert gas atmosphere. The structure of the synthesized materials was characterized by means of FTIR, XRD, TG, SEM and other analysis methods. The effects of the foaming agent oil the structure of PPAS were studied in detail. The experimental results Showed that doping the foaming agent, on one hand, could increase the dehydration speed of pyrolysis processing of PF resin, and decrease the pyrolysis temperatures of it at the same time; on the other hand, the structures changed greatly in crystallite sizes and interlayer spaces for doped pyrolysis materials. Furthermore, when PF resin was doped with the foaming agent, the pyrolysis materials showed the ball or ellipsoid states, however, the un-doped pyrolysis materials showed the bulky and amorphous states with sharp edges and angles. The surface area measurements (BET method) showed that when resin-ZnCl(2) ratio was 1 : 3 (mass ratio), and the speed of heat treatment, 30 degrees C/h, and the pyrolysis temperature, 600 degrees C, the specific surface area could increase to 2150 m(2)center dot g(-1), and the average diameter of the powders got to 11 angstrom. |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/66481] |
专题 | 数学科学-已发表论文 |
推荐引用方式 GB/T 7714 | Lin L. Preparation and structure of porous carbons by pyrolysis of phenol formaldehyde resin[J],2008. |
APA | 林鹭.(2008).Preparation and structure of porous carbons by pyrolysis of phenol formaldehyde resin.. |
MLA | 林鹭."Preparation and structure of porous carbons by pyrolysis of phenol formaldehyde resin".(2008). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论