Influence of interface diffusion between Al substrate and TiO2 film on photocatalytic activity | |
Zhang Wei ; Wang Shu-Liang ; Ma Yun-Qing ; Wang Cui-Ping ; Liu Xing-Jun ; Zhang W(张文) | |
2007-09 | |
关键词 | VISIBLE-LIGHT PHOTOCATALYSIS THIN-FILMS METHYLENE-BLUE TITANIUM GLASS |
英文摘要 | TiO2 nano-crystalline films on Al substrate were prepared from tetra-n-butyl titanate by sol-gel method. The synthesized TiO2 films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The photodegradation activity of methylene blue (MB) solutions under UV irradiation was studied. The results indicated that the TiO2 particles could be built up from crystallites ranging from 10 nm to 20 nm and had a dense bonding. The interface diffusion between TiO2 and Al substrate takes place at calcination temperature of 450 degrees C for 30 min and Al element diffuses into TiO2 film from Al substrate, forming a diffusion layer with a thickness of about 75 nm. The interface diffusion between TiO2 and Al substrate leaded to the inferior photocatalytic activity. The influence of Al substrate on photodegradation activity of MB solutions became less and less as the thickness of the thin film increased. |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/66243] |
专题 | 数学科学-已发表论文 |
推荐引用方式 GB/T 7714 | Zhang Wei,Wang Shu-Liang,Ma Yun-Qing,et al. Influence of interface diffusion between Al substrate and TiO2 film on photocatalytic activity[J],2007. |
APA | Zhang Wei,Wang Shu-Liang,Ma Yun-Qing,Wang Cui-Ping,Liu Xing-Jun,&张文.(2007).Influence of interface diffusion between Al substrate and TiO2 film on photocatalytic activity.. |
MLA | Zhang Wei,et al."Influence of interface diffusion between Al substrate and TiO2 film on photocatalytic activity".(2007). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论