甲基丙烯酸酯嵌段共聚物的合成与表征; SYNTHESIS AND CHARACTERIZATION of BLOCKCOPOLYMERIZATION of METHACRYLATE | |
戴李宗 ; 邹友思 ; 郑洪涛 ; 林国良 ; 潘容华 | |
1998 | |
关键词 | 阴离子聚合 甲基丙烯酸酯 嵌段共聚物 聚合物结构 anionic polymerization methacrylate block copolymer polymer structure |
英文摘要 | 研究了MMA和C7~9MA的阴离子共聚合,得到了A-b型嵌段共聚物。讨论了嵌段顺序、温度、引发剂及PC7~9MA-活性链长对MMA嵌段共聚的影响,认为,当第一嵌段单体为C7~9MA,T=-20℃,[I]=5.0~5.4x10-2MOl/l,Mn(PC7~9MA-)<1.6x104时,有利于PC7~9MA-b-PMMA嵌段共聚物的合成;采用gPC、Ir、nMr对所得嵌段共聚物进行了表征。; The anionic block copolymerization MMA and C7 ̄9Methacrylate(C7 ̄9MA) was studied using nBuLi as initiator.PC7 ̄9MAbPMMA copolymer was obtained.The inFluence of monomer sequence, temperature, initiator and active chain length of PC7 ̄9MA- were discussed on block copolymerization.When T=-20 ℃,=0.50 ̄0.54×10-2 mol/L, C7 ̄9MA as First monomer, PC7 ̄9MA- with n ̄ 1.6×104 was Favorable to the synthesis of PC7 ̄9MA bPMMA block copolymer.The molecular weight and molecular weight distribution of copolymer were measured by GPC.The structure of block copolymer was characterized by FTIR and 1HNMR.; 国家自然科学基金 |
语种 | zh_CN |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/107513] |
专题 | 化学化工-已发表论文 |
推荐引用方式 GB/T 7714 | 戴李宗,邹友思,郑洪涛,等. 甲基丙烯酸酯嵌段共聚物的合成与表征, SYNTHESIS AND CHARACTERIZATION of BLOCKCOPOLYMERIZATION of METHACRYLATE[J],1998. |
APA | 戴李宗,邹友思,郑洪涛,林国良,&潘容华.(1998).甲基丙烯酸酯嵌段共聚物的合成与表征.. |
MLA | 戴李宗,et al."甲基丙烯酸酯嵌段共聚物的合成与表征".(1998). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论