VRLA蓄电池技术; Techniques For VRLA Batteries | |
陈体衔 | |
1997 | |
关键词 | VRLA蓄电池 合金 铅膏 装配压力 快速充电 VRLA Battery Alloy Paste Assembling Pressure Rapid Charge |
英文摘要 | 本文就板栅合金、和膏方程、装配压力、快速充电等方面阐述VrlA蓄电池技术。当Pb—CA合金中锡含量超过0.6%时才可能从循环伏安图观察到锡的阳极溶解,才能起克服早期容量损失的作用。通过加酸量改变铅膏密度,然后再通过和膏方程确定加水量。在和膏后期补水调整铅膏密度是不可取的操作。考虑电池充放电过程极板厚度增加将引起装配压力增大,建议初始装配压力设定在40kg/dM--2。我们首次建立变电流间歇充电方法,它是一种快速充电方法。对于完全放电态电池只需充电时间190MIn,则可得92%放电容量。; Techniques For VRLA batteries such as grid alloy paste-mixing equation .assembling pressure and rapid charge were explained.Only when Sn content in Pb-Ca alloy was more than 0.6wt% ,its anodic dissolution of Sn could been observed From cyclic voltammogram and had eFFect to eliminate the premature capacity loss.The wet-paste density was changed by the amount of sulFuric acid and the amount of water in the oxide.It was determined by the paste-mixing equation.Adjusting wet - paste density by adding water towards the end of the mixing was bad operation.Initial assembling pressure was suggested at 40kg/dm2 because assembling pressure would be increased by increment of electrode thickness in the process of charge and discharge.The interrupt charge with variable current had been Firstly established.This was a rapid charge method.Charge time was only 190 minutes For the discharged battery and the discharge capacity of 92% could be obtained. |
语种 | zh_CN |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/107133] ![]() |
专题 | 化学化工-已发表论文 |
推荐引用方式 GB/T 7714 | 陈体衔. VRLA蓄电池技术, Techniques For VRLA Batteries[J],1997. |
APA | 陈体衔.(1997).VRLA蓄电池技术.. |
MLA | 陈体衔."VRLA蓄电池技术".(1997). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论