功率型锂离子电池负极材料TiO_2/石墨烯的制备及其电化学性能研究; Preparation and Electrochemical Performance of TiO_2/GNs Nanocomposite as Anode Materials for Lithium-Ion Batteries | |
秦琳琳 ; 张焕 ; 刘晓静 ; 许剑辉 ; 施一宁 ; 郑明森 ; 董全峰 | |
2012 | |
关键词 | 锂离子电池 负极材料 TiO2 石墨烯 lithium-ion battery anode materials TiO2 graphene |
英文摘要 | 采用无表面活性剂回流法制备了蜂窝状TIO2/石墨烯(gnS)复合材料.扫描电子显微镜(SEM)及透射电子显微镜(TEM)表征结果表明,TIO2颗粒约5~10 nM,均匀地分散在石墨烯的表面.锂电池测试显示,1C充电容量稳定在240.1 MAH.g-1;30C充电容量为169.5 MAH.g-1;当电流调回1C时,其充电容量仍可完全恢复(241.7 MAH.g-1);10C 300周期循环电极容量保持率为89.8%.; The honeycomb-like porous TiO2/graphenes(TiO2/GNs) nanocomposite was prepared by a reflux method.SEM and TEM results showed that nanosized anatase TiO2(about 5--10 nm) were dispersed uniformly on the surface of the GNs.The TiO2/GNs composite showed excellent rate and cycling performance.A stable charge capacity of 169.5 mAh·g-1 was obtained at 30C,and can restore to 241.7 mAh·g-1 while current went back to 1C.The stable charge capacity of TiO2/GNs nanocomposite electrode up to 201.9 mAh·g-1 was achieved at 10C in the first cycle,and could be maintained at 181.4 mAh·g-1 after 300 cycles.; 国家自然科学基金项目(No.200933005;No.02903077);国家973项目(No.2009CB220102)资助;厦门市纯电动汽车重大科技专项(I期)(No.3502Z20121002) |
语种 | zh_CN |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/106645] |
专题 | 化学化工-已发表论文 |
推荐引用方式 GB/T 7714 | 秦琳琳,张焕,刘晓静,等. 功率型锂离子电池负极材料TiO_2/石墨烯的制备及其电化学性能研究, Preparation and Electrochemical Performance of TiO_2/GNs Nanocomposite as Anode Materials for Lithium-Ion Batteries[J],2012. |
APA | 秦琳琳.,张焕.,刘晓静.,许剑辉.,施一宁.,...&董全峰.(2012).功率型锂离子电池负极材料TiO_2/石墨烯的制备及其电化学性能研究.. |
MLA | 秦琳琳,et al."功率型锂离子电池负极材料TiO_2/石墨烯的制备及其电化学性能研究".(2012). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论