	模拟混凝土孔隙液中钢筋电化学腐蚀行为及pH值的影响作用; Effect of pH on the electrochemical corrosion behavior of reinforcing steel in simulated concrete pore solutions
	唐方苗 ; 徐晖 ; 陈雯 ; 杨榕杰 ; 杜荣归 ; 林昌健
	2011-02
关键词	钢筋 模拟混凝土孔隙液 pH 极化曲线 电化学阻抗谱 reinforcing steel simulated concrete pore solution pH polarization curve electrochemical impedance spectroscopy
英文摘要	通讯作者：杜荣归 作者简介：唐方苗(1985-)，男，安徽安庆人，在读硕士，师承杜荣归教授，从事腐蚀电化学研究。; [中文摘要]应用极化曲线法和电化学阻抗技术,结合扫描电子显微镜方法,测试钢筋在模拟混凝土孔隙液中的钝化与去钝化行为,以及溶液pH值对钢筋电化学腐蚀行为的影响作用。结果表明,钢筋在pH值为12.50的模拟液中处于钝态,随着溶液pH值的降低,钢筋的耐蚀性下降。钢筋表面去钝化发生腐蚀的临界pH值在11.12～11.05范围内。[英文摘要]The passivation and depassivation behavior of reinforcing steel in simulated concrete pore solutions(SPS) with different pH values was studied by the polarization curves,electrochemical impedance spectroscopy and scanning electron microscopy.The results indicated that reinforcing steel was in the passive state in the simulated concrete pore solution with pH 12.50.The lower the pH value of solutions,the more unstable the passive film of reinforcing steel.The critical pH value for the localized corrosion of the reinforcing steel in the simulated concrete pore solutions was between 11.12 and 11.05 based on the electrochemical measurements.; 国家自然科学基金资助项目(20473066);国家自然科学基金重点资助项目(50731004);国家科技支撑计划资助项目(2007BAB27B04)
语种	中文
出版者	《功能材料》编辑部
内容类型	期刊论文
源URL	[http://dspace.xmu.edu.cn/handle/2288/12818]
专题	化学化工－已发表论文
推荐引用方式 GB/T 7714	唐方苗,徐晖,陈雯,等. 模拟混凝土孔隙液中钢筋电化学腐蚀行为及pH值的影响作用, Effect of pH on the electrochemical corrosion behavior of reinforcing steel in simulated concrete pore solutions[J],2011.
APA	唐方苗,徐晖,陈雯,杨榕杰,杜荣归,&林昌健.(2011).模拟混凝土孔隙液中钢筋电化学腐蚀行为及pH值的影响作用..
MLA	唐方苗,et al."模拟混凝土孔隙液中钢筋电化学腐蚀行为及pH值的影响作用".(2011).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。