纳米级LiFePO_4材料的水热模板法合成及其性能研究; The Hydrothermal Synthesis of Nanoscale LiFePO_4 and its Electrochemical Performance | |
王思敏 ; 郑明森 ; 董全峰 | |
2008-11 | |
关键词 | 锂离子电池 磷酸铁锂 水热模板法 lithium ion battery LiFePO4 hydrothermal templating synthesis |
英文摘要 | [中文文摘]采用水热模板法合成纳米级LiFePO4材料,改变水热反应中表面活性剂(十六烷基三甲基溴化铵)的比例控制样品颗粒生成的大小.SEM测试表明,合成的LiFePO4晶粒尺寸与表面活性剂的配比密切相关,范围在几十到几百nm之间.充放电试验表明,合成的纳米级LiFePO4材料电极具有优良的电化学性能,其0.1C放电最高比容量可达150 mAh/g,而1C和2C放电比容量也分别有140 mAh/g和126 mAh/g.[英文文摘]The cathode materials of nanosiged LiFePO4 were prepared by hydrothermal templating synthesis.The grain sizes and electrochemical performance of LiFePO4 were controlled by surfactant.It was shown that the grain sizes varied from less than a hundred to hundreds nanometers by the SEM images.In the charge/discharge tests,the discharge capacities of the sample as a lithium ion battery were achieved to 150 mAh/g at 0.1C,140 mAh/g at 1C,and 126 mAh/g at 2C,with good cycling performance.; 国防基础研究项目(XMDX2008176); 省部产学研项目(2007B090400126)资助。 |
语种 | 中文 |
出版者 | 《电化学》编辑部 |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/3217] |
专题 | 化学化工-已发表论文 |
推荐引用方式 GB/T 7714 | 王思敏,郑明森,董全峰. 纳米级LiFePO_4材料的水热模板法合成及其性能研究, The Hydrothermal Synthesis of Nanoscale LiFePO_4 and its Electrochemical Performance[J],2008. |
APA | 王思敏,郑明森,&董全峰.(2008).纳米级LiFePO_4材料的水热模板法合成及其性能研究.. |
MLA | 王思敏,et al."纳米级LiFePO_4材料的水热模板法合成及其性能研究".(2008). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论