聚碳硅烷氮化热解法制备SiNO陶瓷; Preparation of SiNO Ceramic by Pyrolysis Nitridation of Polycarbosilane | |
丁绍楠 ; 刘玲 ; 李风萍 ; 胡志明 ; 刘星煜 ; 刘安华 | |
2015-11-28 | |
关键词 | 聚碳硅烷 氮化热解法 SiNO陶瓷 polycarbosilane pyrolysis nitridation SiNO ceramic |
英文摘要 | 系统研究了热解和氧化条件对聚碳硅烷氮化热解法制备SInO陶瓷的影响.研究发现,氮化脱碳反应主要发生在800℃之前,且脱碳彻底,碳质量分数低于1%;在氮气气氛下继续烧成,最终生成陶瓷的氮质量分数可达35.65%.氮化前对聚碳硅烷进行氧化交联可提高陶瓷产率至61.84%,但是产物中氮质量分数显著降低到20%以下,产物为无定型态的SInO陶瓷.; SiNO ceramic has very excellent comprehensive properties and is one of the best candidates for ceramic matrix composites.In this work,influences of pyrolysis and curing conditions on the SiNO ceramic prepared with pyrolysis nitridation are systematically studied.The results show that decarbonization is completed before 800 ℃ with carbon residue lower than 1%(by mass).After pyrolysis in N2,nitrogen content is as high as 35.65%(by mass).Oxidation curing before ammonolysis can improve ceramic yield.The ceramic yield is 61.84%(by mass)but the nitrogen content decreases significantly(below 20%)by mass,and the product is amorphous SiNO ceramic.Therefore,high-yield and low-carbon-content SiNO ceramic can be prepared with pyrolysis nitridation of polycarbosilane.; 国家自然科学基金(51002127) |
语种 | zh_CN |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/98511] ![]() |
专题 | 材料学院-已发表论文 |
推荐引用方式 GB/T 7714 | 丁绍楠,刘玲,李风萍,等. 聚碳硅烷氮化热解法制备SiNO陶瓷, Preparation of SiNO Ceramic by Pyrolysis Nitridation of Polycarbosilane[J],2015. |
APA | 丁绍楠,刘玲,李风萍,胡志明,刘星煜,&刘安华.(2015).聚碳硅烷氮化热解法制备SiNO陶瓷.. |
MLA | 丁绍楠,et al."聚碳硅烷氮化热解法制备SiNO陶瓷".(2015). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论