	结构化增韧层增韧RTM复合材料预成型体的渗透特性; Permeability of toughened RTM composite preforms by structural toughening layer
	刘刚 ; 张朋 ; 李伟东 ; 胡晓兰 ; 包建文 ; 益小苏
	2014-06-04
关键词	RTM 尼龙无纺布 复合材料 层间增韧 渗透率 RTM nylon nonwoven fabric composites interlaminar toughening permeabiliy
英文摘要	选用尼龙无纺布(POlyAMIdE nOnWOVEn fAbrIC,Pnf)作为结构化增韧层,研究了增韧层的引入对纤维预成型体在树脂传递模塑成型(rTM)工艺过程中渗透特性的影响。结果表明:在径向非饱和流动模式下,层间增韧预成型体沿纤维方向的渗透率为5.2x10-12 M2,略低于非增韧预成型体的7.1x10-12 M2,而沿垂直于纤维方向的渗透率为2.3x10-12 M2,略高于非增韧预成型体的1.6x10-12 M2。此外,层间增韧预成型体的单向饱和流动渗透率为2.6x10-12 M2,较非增韧预成型体的1.9x10-11 M2下降了约1个数量级,z向饱和流动渗透率较非增韧预成型体的1.3x10-13 M2下降至2.5x10-14 M2,同样下降了约1个数量级。对复合材料层间微观形貌的分析结果表明:造成预成型体渗透率下降的主要原因首先是Pnf引入至层间之后将阻碍层间树脂的快速流动,同时增韧层将使层内纤维含量明显升高,由55.3VOl%上升到63.7VOl%。; The nylon nonwoven fabric(Polyamide Nonwoven Fabric,PNF)was selected as structural toughening layer to investigate its effect on the permeability of fiber preforms during resin transfer molding(RTM)process.Results show that under unsaturated radial flow pattern,the permeability of the interlaminar toughened preform along the direction of fiber(5.2×10-12 m2)is lower than that of the untoughened preform(7.1×10-12 m2).On the contrary,the permeability of the toughened preform perpendicular to the fiber direction(2.3×10-12 m2)is higher than that of the untoughened preform(1.6×10-12 m2).Moreover,the unidirectional saturated flow permeability of interlaminar toughened preform is 2.6×10-12 m2,which is much lower than that of untoughened preform(1.9×10-11 m2),decreased by an order of magnitude.The z-directional saturated permeability also dramatically decreases from 1.3×10-13 m2(untoughened preform)to 2.5×10-14 m2,decreased by an order of magnitude.The interlaminar morphology analysis results reveal that the decrease of the permeability of preform mainly results from the inhibition of rapid flow of resin,introduced by PNF as structural layers and the increment of interlaminar fiber contents rising from 55.3vol%to 63.7vol%.; 国家自然科学基金(51203144)
语种	zh_CN
内容类型	期刊论文
源URL	[http://dspace.xmu.edu.cn/handle/2288/98508]
专题	材料学院－已发表论文
推荐引用方式 GB/T 7714	刘刚,张朋,李伟东,等. 结构化增韧层增韧RTM复合材料预成型体的渗透特性, Permeability of toughened RTM composite preforms by structural toughening layer[J],2014.
APA	刘刚,张朋,李伟东,胡晓兰,包建文,&益小苏.(2014).结构化增韧层增韧RTM复合材料预成型体的渗透特性..
MLA	刘刚,et al."结构化增韧层增韧RTM复合材料预成型体的渗透特性".(2014).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。