| Fe掺杂和热处理对SiC纤维微结构与电性能影响规律的研究; Effect of iron doping and heat treating on specific resistivity of SiC fibre | |
| 陆雪川 ; 陈立富 ; 李思维 ; 唐学原 ; 李华展 ; 丁马太 | |
| 2014-04-15 | |
| 关键词 | SiC纤维 Fe掺杂 热处理 电阻率 微观结构 silicon carbide fibre iron doping heat treatment electrical resistivity microstructure |
| 英文摘要 | 利用氧化交联技术制备了含铁量分别为0,1%,2%(质量分数)的3种碳化硅纤维,并将其置于氩气环境进行了不同温度、不同时间的热处理。研究了fE掺杂及热处理对于SIC纤维微观结构及电阻特性的影响规律。结果表明,在fE掺杂和热处理的协同作用下,该碳化硅纤维电阻率可由13 847Ω·CM连续降低至6Ω·CM。利用统计理论“相关分析“算法研究纤维微观结构与电阻率关系的结果表明,在实验条件下,β-SIC的晶粒尺寸对纤维电阻率的影响最为显著。根据实验结果,提出了该含铁SIC纤维微结构演化的模型。; Silicon carbide fibers doped with iron of 0-2wt% were prepared from iron-containing polycarbosilane by using oxygen-curing method.The as-prepared fibers were heated in high purity argon from 700to 1 100℃up to 100h.With the change of treating parameters,the specific resistivity of the fibers decreased from 13 847to 6Ω ·cm while the content and crystallinity of the multi-phases in fibers varied non-monotonically.Linear relationship between microstructure with electrical property was evaluated using pearson coefficients.Among the tested factors,grain size ofβ-SiC was the most relevant to specific resistivity,effect of iron content was subordinate.Mechanism on microstructure evolution of the iron-doped fiber was proposed.; 国家自然科学基金面上资助项目(51072169);国家自然科学基金青年基金资助项目(51302234); 深圳市科创委科技知识创新计划资助项目(JCYJ20130329150151152) |
| 语种 | zh_CN |
| 内容类型 | 期刊论文 |
| 源URL | [http://dspace.xmu.edu.cn/handle/2288/98445]  |
| 专题 | 材料学院－已发表论文 |
| 推荐引用方式 GB/T 7714 | 陆雪川,陈立富,李思维,等. Fe掺杂和热处理对SiC纤维微结构与电性能影响规律的研究, Effect of iron doping and heat treating on specific resistivity of SiC fibre[J],2014. |
| APA | 陆雪川,陈立富,李思维,唐学原,李华展,&丁马太.(2014).Fe掺杂和热处理对SiC纤维微结构与电性能影响规律的研究.. |
| MLA | 陆雪川,et al."Fe掺杂和热处理对SiC纤维微结构与电性能影响规律的研究".(2014). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论