Multiaxial fatigue behavior of Ni-based superalloy GH4169 at 650 °C | |
Shang DG(尚德广) ; Sun GQ(孙国芹) | |
中文摘要 | The fatigue behavior of a Ni-based superalloy GH4169 was investigated using thin tubular specimens under multiaxial loading at 650 °C. Fatigue testing included multiaxial constant amplitude loading and variable amplitude block loading. The test results showed that the characteristics of cyclic hardening or softening depended on the strain loading paths, the sequence of the loading paths, and the loading parameters. Additional hardening due to non-proportional cyclic loading was still present at 650 °C, which caused the fatigue life to decrease. The sequence of the loading paths has an obvious influence on fatigue life, as shown by the increase in loading strain amplitude. Creep effect was observed in the multiaxial fatigue process at high temperature, and an increase in the number of cycles gradually strengthened the creep effect. Fractography showed intergranular fracture phenomena, which reflects the fatigue-creep behavior under non-proportional cyclic loading at high temperature. ? 2006 Elsevier B.V. All rights reserved. |
原文出处 | http://dlib.edu.cnki.net/kns50/download.aspx?filename=Jh2c0hHTvllWvEUavFDVplldsl3Z0dUWhNVRrUWMvJjMSVmVztWVol1Vyt0bwd2K2dWdnlWdCZEeFNGe14WV5YWT3ITeFtianJXaRFWc0dFcZxERhRWWkNnM0MEe3oWarMFOJt0U1YUTYJzKMhGSWxmQvg2VxhlM&tablename=CJFD2009&dflag=pdfdown 全文链接 |
内容类型 | 期刊论文 |
源URL | |
专题 | 北京工业大学 |
推荐引用方式 GB/T 7714 | Shang DG,Sun GQ. Multiaxial fatigue behavior of Ni-based superalloy GH4169 at 650 °C[J]. |
APA | 尚德广,&孙国芹. |
MLA | 尚德广,et al."Multiaxial fatigue behavior of Ni-based superalloy GH4169 at 650 °C". |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论