Effects of Ta Content and Sintering Temperature on Phase Composition,Microstructure and Electrical Properties of(Li,K,Na)(Nb_(1-x)Ta_x)O_3 Lead-free Piezoelectric Ceramics | |
ZHEN Yuhua ; LI Jingfeng ; ZHEN Yuhua ; LI Jingfeng | |
2016-03-30 ; 2016-03-30 | |
关键词 | lead-free piezoelectric,crystal structure,microstructure electric properties TQ174.1 |
其他题名 | Effects of Ta Content and Sintering Temperature on Phase Composition,Microstructure and Electrical Properties of(Li,K,Na)(Nb_(1-x)Ta_x)O_3 Lead-free Piezoelectric Ceramics |
中文摘要 | (Li,K,Na)(Nb_(1-x)Ta_x)O_3(x=0,0.10,0.15,0.2) lead-free piezoelectric ceramics were fabricated via solid-state sintering.The effects of Ta content and sintering temperature on the microstructure,phase structure and electrical properties were investigated.The results show that Ta doping can induce the phase transition from orthorhombic to tetragonal symmetry in the Ta content range from 0.10 to 0.15.Also,Ta can efficiently suppress the grain growth until Ta content increases up to 0.15,and a relatively high sintering temperature can cause an abnormal grain growth at Ta content of<0.20.Also,the results indicate that a bimodal grain size distribution with dense microstructure can lead to a higher dielectric constant.Moreover,a relatively high piezoelectric coefficient d_(33) of 206 pC/N is obtained at Ta content of 0.15,which is probably due to the polymorphic phase transition.; (Li,K,Na)(Nb_(1-x)Ta_x)O_3(x=0,0.10,0.15,0.2) lead-free piezoelectric ceramics were fabricated via solid-state sintering.The effects of Ta content and sintering temperature on the microstructure,phase structure and electrical properties were investigated.The results show that Ta doping can induce the phase transition from orthorhombic to tetragonal symmetry in the Ta content range from 0.10 to 0.15.Also,Ta can efficiently suppress the grain growth until Ta content increases up to 0.15,and a relatively high sintering temperature can cause an abnormal grain growth at Ta content of<0.20.Also,the results indicate that a bimodal grain size distribution with dense microstructure can lead to a higher dielectric constant.Moreover,a relatively high piezoelectric coefficient d_(33) of 206 pC/N is obtained at Ta content of 0.15,which is probably due to the polymorphic phase transition. |
语种 | 英语 ; 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.lib.tsinghua.edu.cn/ir/item.do?handle=123456789/141753] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | ZHEN Yuhua,LI Jingfeng,ZHEN Yuhua,et al. Effects of Ta Content and Sintering Temperature on Phase Composition,Microstructure and Electrical Properties of(Li,K,Na)(Nb_(1-x)Ta_x)O_3 Lead-free Piezoelectric Ceramics[J],2016, 2016. |
APA | ZHEN Yuhua,LI Jingfeng,ZHEN Yuhua,&LI Jingfeng.(2016).Effects of Ta Content and Sintering Temperature on Phase Composition,Microstructure and Electrical Properties of(Li,K,Na)(Nb_(1-x)Ta_x)O_3 Lead-free Piezoelectric Ceramics.. |
MLA | ZHEN Yuhua,et al."Effects of Ta Content and Sintering Temperature on Phase Composition,Microstructure and Electrical Properties of(Li,K,Na)(Nb_(1-x)Ta_x)O_3 Lead-free Piezoelectric Ceramics".(2016). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论