Research on technology and batch formula of sintering municipal sewage sludge for manufacturing haydite | |
Jin Yi-ying ; Du Xin ; Wang Zhi-yu ; Wang Xing-run ; Nie Yong-feng | |
2010-10-12 ; 2010-10-12 | |
关键词 | Experimental/ sewage treatment sintering sludge treatment/ municipal sewage sludge sintering technology haydite anhydration sintering compression strength hygroscopic coefficient temperature 350 C time 20 min temperature 1060 C time 15 min/ E3040 Public utilities E1525 Industrial processes E1520J Powder technology E0230 Environmental issues/ temperature 6.2315E+02 K time 1.2E+03 s temperature 1.33315E+03 K time 9.0E+02 s |
中文摘要 | Sintering technology and batch formula of "anhydration-sintering" for manufacturing haydite in municipal sewage sludge were studied. The impacts of process conditions on product compression strength, hygroscopic coefficient and density were analyzed. Sintering temperature had important influence on haydite. The fitting sintering temperature was decided by the sludge percentage in batch formula, because of sludge's low melting point, low intensity and fluxing action. The best technical scheme was as followed: the sludge percentage could reach 80% at most and the sintering process was warm-up at 350 degrees C for 20 minutes and sintering at 1060 degrees C for 15 minutes. |
语种 | 中文 |
出版者 | Editorial Board of China Environmental Science ; China |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/79799] ![]() |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Jin Yi-ying,Du Xin,Wang Zhi-yu,et al. Research on technology and batch formula of sintering municipal sewage sludge for manufacturing haydite[J],2010, 2010. |
APA | Jin Yi-ying,Du Xin,Wang Zhi-yu,Wang Xing-run,&Nie Yong-feng.(2010).Research on technology and batch formula of sintering municipal sewage sludge for manufacturing haydite.. |
MLA | Jin Yi-ying,et al."Research on technology and batch formula of sintering municipal sewage sludge for manufacturing haydite".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论