PVDF based ion exchange membrane for all vanadium redox flow battery | |
Long Fei ; Fan Yong-sheng ; Wang Bao-guo | |
2010-10-12 ; 2010-10-12 | |
关键词 | Practical Experimental/ Fourier transform spectroscopy infrared spectroscopy ion exchange membranes permeability polymers secondary cells vanadium/ ion exchange membrane vanadium redox flow battery polyvinylidene fluoride PVDF ion exchange capacity vanadium ion permeability ratio sodium allylsulfonate membrane FT-IR analysis membrane formation self-discharge test vanadium ion permeation rate open circuit condition V/ A8630F Secondary cells A8230H Chemical exchanges (substitution, atom transfer, abstraction, disproportionation, and group exchange) B8410E Secondary cells/ V/el |
中文摘要 | Three kinds of polyvinylidene fluoride (PVDF) based ion exchange membranes were prepared, their area resistance,ion exchange capacity (IEC), water content and vanadium ion permeability ratio were compared. The PVDF-sodium allylsulfonate (SAS) membrane prepared with a homogeneous solution of PVDF and SAS had the lowest area resistance of 1.2 Omega middot cm/sup 2/, its IEC was 1.16 mmol/g. FT-IR analysis showed that the C = C bond of SAS polymerized after long time under high temperature and formed inter network structure with PVDF during the processes of the membranes formation. Self-discharge test showed that the vanadium ions permeation rate of the prepared membrane was below 8.8 * 10/sup -3/ V/h at open circuit condition. |
语种 | 中文 |
出版者 | Hunan Light Industry Research Institute ; China |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/79474] ![]() |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Long Fei,Fan Yong-sheng,Wang Bao-guo. PVDF based ion exchange membrane for all vanadium redox flow battery[J],2010, 2010. |
APA | Long Fei,Fan Yong-sheng,&Wang Bao-guo.(2010).PVDF based ion exchange membrane for all vanadium redox flow battery.. |
MLA | Long Fei,et al."PVDF based ion exchange membrane for all vanadium redox flow battery".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论