	Microstructure and microwave dielectric properties of Ba5Nb4O15-BaWO4 composite ceramics
	Zhuang, Hao ; Yue, Zhenxing ; Zhao, Fei ; Pei, Jing ; Li, Longtu
	2010-10-12 ; 2010-10-12
关键词	Ceramics Electriconic properties TEM COMPLEX PERMITTIVITY CRYSTAL-STRUCTURE TEMPERATURE PEROVSKITES TUNGSTATES RESONATORS SYSTEM BAWO4 A=BA CA Chemistry, Physical Materials Science, Multidisciplinary Metallurgy & Metallurgical Engineering
中文摘要	Microwave dielectric composite ceramics with compositions of (1-x)Ba5Nb4O15-xBaWO(4) (x=0-1) were prepared by firing the mixture of Ba5Nb4O15 and BaWO4. The sintering temperature of the composite ceramics was reduced from 1400 to 1100 degrees C with increasing BaWO4 content. XRD patterns indicate that Ba5Nb4O15 and BaWO4 coexisted and no secondary phase was detected in sintered bodies. The composite ceramics have the finer grained microstructure compared with the pure Ba5Nb4O15 ceramics. TEM observation and EDS analysis reveal that a very thin interfacial area (similar to 60nm in width) was formed due to the limited solid solution between Ba5Nb4O15 and BaWO4 grains. With increasing BaWO4 (from x=0 to x=0.65), the dielectric constants (epsilon(r)) and the temperature coefficient of resonant frequency (tau(f)) of the ceramics decrease from 39.2 to 16.9 and from +78 to -4.3 ppm/degrees C, respectively, while the quality factors (Q x fvalue) increase from 26,000 to 56,700 GHz. The samples with x=0.54-0.65 sintered at 1100 degrees C exhibit good microwave dielectric properties: epsilon(r)=21.0-16.9, Q x f=49,500-56,700 GHz, and tau(f)=8.9--4.3 ppm/degrees C. (C) 2008 Elsevier B.V. All rights reserved.
语种	英语 ; 英语
出版者	ELSEVIER SCIENCE SA ; LAUSANNE ; PO BOX 564, 1001 LAUSANNE, SWITZERLAND
内容类型	期刊论文
源URL	[http://hdl.handle.net/123456789/78363]
专题	清华大学
推荐引用方式 GB/T 7714	Zhuang, Hao,Yue, Zhenxing,Zhao, Fei,et al. Microstructure and microwave dielectric properties of Ba5Nb4O15-BaWO4 composite ceramics[J],2010, 2010.
APA	Zhuang, Hao,Yue, Zhenxing,Zhao, Fei,Pei, Jing,&Li, Longtu.(2010).Microstructure and microwave dielectric properties of Ba5Nb4O15-BaWO4 composite ceramics..
MLA	Zhuang, Hao,et al."Microstructure and microwave dielectric properties of Ba5Nb4O15-BaWO4 composite ceramics".(2010).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。