	聚3-羟基丁酸酯薄膜结晶的ATR-FTIR研究
	王震 ; 杨睿 ; 徐军 ; 谢续明 ; WANG Zhen ; YANG Rui ; XU Jun ; XIE Xuming
	2010-06-10 ; 2010-06-10
关键词	PHB 薄膜 基板 分子取向 ATR-FTIR PHB, Thin films, Substrate, Molecular orientation, ATR-FTIR TQ320.721
其他题名	ATR-FTIR STUDIES ON THE EFFECT OF THICKNESS ON THE CRYSTALLIZATION OF POLY(3-HYDROXYBUTYRATE) THIN FILMS
中文摘要	使用匀胶机(spincoater),通过溶液铸膜的方法,在铝箔基板上制备出具有不同厚度的聚3羟基丁酸酯(PHB)薄膜.20℃室温条件下,通过衰减全反射傅立叶红外光谱(ATRFTIR)原位观测了不同厚度薄膜的结晶过程,并通过偏光ATRFTIR对薄膜中PHB分子的取向进行了研究.ATRFTIR原位观测结果显示,PHB在薄膜中的结晶速率以及结晶度均随着薄膜厚度的减小而逐渐降低;同时,偏光ATRFTIR测试结果表明,随膜厚减小,薄膜中结晶部分的PHB分子逐渐倾向于沿垂直于基板表面方向取向,膜越薄,倾向越明显.可以认为,PHB分子与基板间的相互作用以及扩散控制结晶导致了上述现象的产生.; The crystallization of (poly(3-hydroxybutyrate)) (PHB) thin films was observed in situ by ATR (attenuated total reflection)-FTIR.The PHB films with different thickness were prepared by means of spin-coating on Al substrates,and then the isothermal crystallization of the PHB films at 20℃ was investigated in situ by ATR-FTIR.The results revealed that the crystallization kinetics of PHB films was affected obviously by the film thickness. A reduction in the crystallinity as well as in the rate of crystallization was found with decreasing the film thickness, because the crystallization occurred under constrained geometry conditions.In addition,the effect of film thickness on the orientation of the molecules of the PHB crystals in the films was investigated by polarized ATR-FTIR.The results imply a preferred orientation of the polymer chain axis in the crystals along the surface-normal direction of the films. The thinner the film thickness,the more the preferred crystalline chain orientation perpendicular to the film surface is.; 国家自然科学基金(基金号20174022); 重大研究计划“理论物理学及其交叉科学若干前沿问题”子课号90103035); 重点资金(基金号10334020)资助项目
语种	中文 ; 中文
内容类型	期刊论文
源URL	[http://hdl.handle.net/123456789/64602]
专题	清华大学
推荐引用方式 GB/T 7714	王震,杨睿,徐军,等. 聚3-羟基丁酸酯薄膜结晶的ATR-FTIR研究[J],2010, 2010.
APA	王震.,杨睿.,徐军.,谢续明.,WANG Zhen.,...&XIE Xuming.(2010).聚3-羟基丁酸酯薄膜结晶的ATR-FTIR研究..
MLA	王震,et al."聚3-羟基丁酸酯薄膜结晶的ATR-FTIR研究".(2010).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。