高通量ZSM-5填充硅橡胶复合膜渗透汽化性能研究 | |
展侠 ; 李继定 ; 操建华 ; 黄军其 ; 陈翠仙 ; ZHAN Xia ; LI Jiding ; CAO Jianhua ; HUANG Junqi ; CHEN Cuixian | |
2010-06-10 ; 2010-06-10 | |
关键词 | ZSM-5 聚二甲基硅氧烷(PDMS) 渗透通量 优先透醇 渗透汽化 ZSM-5 PDMS permeation flux ethanol perm-selective pervaporation TQ028.8 |
其他题名 | Pervaporation performance of ZSM-5 filled silicone composite membranes with high flux |
中文摘要 | 以硅铝比为360的ZSM-5型沸石对聚二甲基硅氧烷(PDMS)进行填充,以聚偏氟乙烯(PVDF)为支撑层,制备了ZSM-5填充PDMS/PVDF复合膜,用于渗透汽化乙醇/水混合物的分离.研究了沸石填充量、操作温度、进料液浓度对乙醇/水的渗透汽化分离性能的影响,发现该复合膜较文献报道中的沸石填充膜,其渗透通量有了明显的提高,在50℃沸石填充量为40%时,对乙醇的分离因子为11.7,其渗透通量达到749.8 g/(m2.h).随着操作温度的升高或料液中乙醇浓度升高,渗透通量增大,分离因子下降.; Zeolite filled polydimethylsiloxane(PDMS) composite membrane was prepared by incorporation of ZSM-5 particles with Si/Al ratio of 360 into PDMS solution which was cast onto polyvinylidene fluoride(PVDF) porous membranes.The resulted zeolite filled PDMS/PVDF composite membranes were applied for the pervaporation of ethanol/water mixtures.The effect of zeolite content,operation temperature and ethanol concentration in feed on pervaporation performance of ethanol/water mixtures was investigated.It was found that the permeation flux was enhanced significantly compared with that reported in literatures.As the zeolite content was 40wt%,the permeation flux reached 749.8 g/(m2·h) with separation factor of 11.7 at 50 ℃.As the operation temperature or ethanol concentration in feed increased,the permeation flux increased and the separation factor followed the reversed order.; 国家“973”项目(2003CB615701); 国家自然科学基金项目(20576059,20676067,20736003); 国家“863”计划项目(2007AA06Z317); 中石化科技开发研究基金(X505002) |
语种 | 中文 ; 中文 |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/64280] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | 展侠,李继定,操建华,等. 高通量ZSM-5填充硅橡胶复合膜渗透汽化性能研究[J],2010, 2010. |
APA | 展侠.,李继定.,操建华.,黄军其.,陈翠仙.,...&CHEN Cuixian.(2010).高通量ZSM-5填充硅橡胶复合膜渗透汽化性能研究.. |
MLA | 展侠,et al."高通量ZSM-5填充硅橡胶复合膜渗透汽化性能研究".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论