| Fe-B/Fe_3O_4纳米复合粒子的吸波性能研究 | |
| 李婷 ; 唐瑞鹤 ; 于荣海 ; LI Ting ; TANG Rui-he ; YU Rong-hai | |
| 2010-06-10 ; 2010-06-10 | |
| 关键词 | 磁性复合粒子 Fe-B 吸波性能 magnetic composite nanoparticles Fe-B microwave absorption properties TB383.1 |
| 其他题名 | Microwave Absorption Properties of Core/ Shell-type Fe-B/Fe_3O_4 Nanoparticles |
| 中文摘要 | 采用NaBH4溶液还原FeCl3的方法制备Fe-B颗粒,并在Ar/O2气氛下干燥,使其表面不完全氧化,得到了Fe-B/Fe3O4纳米复合粒子。该粒子具有清晰的核壳结构,内核Fe-B尺寸约为20~50 nm,外壳Fe3O4厚度约为3 nm。将样品与石蜡按质量比1∶1制成同轴样品,测试其2~18 GHz下的电磁参数并进行分析计算,研究发现,由于偶极子极化、自然共振和涡流损耗,该纳米复合粒子粉末具有优良的吸波性能,其反射损耗RL在频率为12.0GHz的时候达到最小值-31 dB,RL值低于-20 dB(即吸收率高于99%)的频率范围为10.1~14.2 GHz。; Fe-B/Fe3O4 nanoparticles were prepared by chemical reduction with borohydride and dried in Ar/O2 atmosphere.The nanoparticles have clear core/shell structure with the Fe-B core of 20-50 nm and the Fe3O4 shell of 3 nm.The nanoparticles were mixed with paraffin(1∶1 in mass ratio) to form a ring sample for measuring the complex electromagnetic parameters in the frequency range of 2-18 GHz.It is found that the composite exhibits excellent microwave absorption properties(reflection loss <-20 dB) in the range 10.1-14.2 GHz due to the orientational polarization,natural resonance and eddy current loss.; 国家自然科学基金(50771058); 国家杰出青年基金(50525101) |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/61710]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 李婷,唐瑞鹤,于荣海,等. Fe-B/Fe_3O_4纳米复合粒子的吸波性能研究[J],2010, 2010. |
| APA | 李婷,唐瑞鹤,于荣海,LI Ting,TANG Rui-he,&YU Rong-hai.(2010).Fe-B/Fe_3O_4纳米复合粒子的吸波性能研究.. |
| MLA | 李婷,et al."Fe-B/Fe_3O_4纳米复合粒子的吸波性能研究".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论