| 磨粒粒径对Si_3N_4结构陶瓷冲蚀磨损性能的影响 | |
| 鲍崇高 ; 潘伟 ; 苗赫濯 ; 齐龙浩 ; Bao Chonggao ; Pan Wei ; Miao Hezhuo ; Qi Longhao | |
| 2010-06-10 ; 2010-06-10 | |
| 关键词 | 冲蚀磨损 磨粒粒径 Cr15Mo3 高铬铸铁 Si3N4结构陶瓷 erosion abrasive particle size Cr15Mo3 high chromium cast ion Si_3N_4 ceramics TQ174.1 |
| 其他题名 | Effect of Abrasive Particle Size on Anti-Abrasion Performance of Si_3N_4 Ceramics |
| 中文摘要 | 以冲蚀磨损工况下的典型应用材料Cr15Mo3高铬铸铁为对比材料,采用转盘式液-固双相流试验机研究了不同SiC磨粒粒径对Si3N4结构陶瓷抗冲蚀磨损性能的影响,分析了试验材料冲蚀磨损的微观失效机制.研究结果表明:在各种粒径磨粒的冲蚀磨损条件下,Cr15Mo3铸铁的冲蚀磨损率都比Si3N4结构陶瓷的高,Si3N4结构陶瓷的抗冲蚀磨损能力是Cr15Mo3铸铁的20倍左右;粗颗粒磨料冲蚀条件下试验材料的体积损失比细颗粒磨料冲蚀条件下的大,即磨粒越粗冲蚀磨损越严重;在微观上,Cr15Mo3的腐蚀坑、冲蚀坑多,基体材料冲刷磨损严重,W型失效形貌明显,而Si3N4结构陶瓷的冲蚀磨损面比较光滑,材料失效主要是晶界粘结相失去多所致;结构致密、晶粒细小并有细小柱状晶的存在等是Si3N4结构陶瓷抗冲蚀磨损性能优异的主要原因.; Erosion resistance of Si_3N_4 structure ceramics was investigated using water slurry with different SiC particle sizes on a liquid-solid dual phase erosion tester with a rotation disk,and Cr15Mo3 high chromium cast iron was taken as a contrast in the test.The erosive mechanism of the test materials in slurry erosion was also discussed.The results show that the slurry erosion of Cr15Mo3 is more severe than that of Si_3N_4 with varying abrasive particles diameters.The erosive resistance of Si_3N_4 ceramics is 20 times higher than that of Cr15Mo3 cast iron.The lost volume of the test materials eroded by larger particles is larger than that by smaller ones.SEM observation reveals that there exist more abrasive and erosive pits on worn surface of Cr15Mo3 iron,compared with smooth worn surface of Si_3N_4,and W-shaped fault feature appears on some failure surfaces of Cr15Mo3 iron.The better erosive resistance of Si_3N_4 lies in its finer granular and column grains,higher density and hardness.; 国家高技术研究发展计划重点资助项目(2001AA333030); 中国博士后科学研究基金资助项目(中博字2003(03)) |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/61622]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 鲍崇高,潘伟,苗赫濯,等. 磨粒粒径对Si_3N_4结构陶瓷冲蚀磨损性能的影响[J],2010, 2010. |
| APA | 鲍崇高.,潘伟.,苗赫濯.,齐龙浩.,Bao Chonggao.,...&Qi Longhao.(2010).磨粒粒径对Si_3N_4结构陶瓷冲蚀磨损性能的影响.. |
| MLA | 鲍崇高,et al."磨粒粒径对Si_3N_4结构陶瓷冲蚀磨损性能的影响".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论