| 乐斌 ; 唐子龙 ; 张中太 ; Le Bin ; Tang Zilong ; Zhang Zhongtai | |
| 2010-06-10 ; 2010-06-10 | |
| 关键词 | 锂离子电池 正极材料 LiFePO4 碳热还原 lithium battery cathode LiFePO4 carbothermal reduction TB383.3 |
| 其他题名 | LiFePO_4 Prepared by Carbothermal Reduction Method |
| 中文摘要 | 以碳热还原法为原理,采用Fe2O3、Li2CO3、NH3H2PO4和碳黑为原料,以一定计量比和顺序混合,经过球磨、干燥、造粒、预烧、烧成等几道工序,制备出黑色的LiFePO4/C粉末。利用化学分析、XRD、SEM等手段研究了工艺流程对合成产物晶体结构、表面形貌的影响。利用合成材料组装电池,通过充放电试验测试电化学性能。结果表明,以0.1C速率充放电,首次充放电容量在150mAh/g。从长远看来,这种低成本,工艺简单,绿色无污染的合成方法很具有工业实用化生产价值。; LiFePO4/C powder was synthesized using carthothermal method with Fe2O3,Li2CO3,NH4H2PO4 and carbon.The effect of technology,synthesis temperature and time on the crystal structure and surface morphology was investigated by chemical analysis,XRD and SEM.LiFePO4 was used to assemble coincell and its electrochemical performances were tested with the charge and discharge experiment.The results showed that its first change/discharge magnitude are 150 mAh/g at the rate of 0.1 C.In long views,this low cost,simple,environment harmless method is suitable for industry producing; 国家自然科学基金(50372033); 清华大学基础研究基金(JC2003040) |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/61349]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 乐斌,唐子龙,张中太,等. LiFePO_4固相碳热合成法研究[J],2010, 2010. |
| APA | 乐斌,唐子龙,张中太,Le Bin,Tang Zilong,&Zhang Zhongtai.(2010).LiFePO_4固相碳热合成法研究.. |
| MLA | 乐斌,et al."LiFePO_4固相碳热合成法研究".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论