| 空冷贝氏体钢的残余应力对屈服强度的影响 | |
| 王勇围 ; 许峰云 ; 白秉哲 ; 方鸿生 ; WANG Yong-wei ; XU Feng-yun ; BAI Bing-zhe ; FANG Hong-sheng | |
| 2010-06-10 ; 2010-06-10 | |
| 关键词 | 贝氏体 超强螺纹钢筋 屈服强度 残余应力 bainite super-strength screw-thread steel yield strength residual stress TG142.15 |
| 其他题名 | Effect of residual stress on yield strength of air-cooled bainitic steel |
| 中文摘要 | 测量了贝氏体超强精轧螺纹钢筋正火态和低温回火后的屈服强度,结果表明,正火态的屈服强度值较低,经300℃低温回火后屈服强度提高约230MPa。同时用盲孔法测定了该两种状态下的表层残余应力值,正火态高达270MPa左右,低温回火后表层残余应力降至70MPa左右,正火态低的屈服强度可能与试样内部高的残余拉应力有关;低温回火能显著降低残余应力,有效提高贝氏体超强钢筋的屈服强度。; Yield strength(R_(0.2)) of a precision-rolled bainitic screw-thread steel(BSS) normalized and tempered at low temperature was measured,results show that R_(0.2) of the BSS after normalizing is relatively lower and it can increase by 230MPa tempered at 300℃.Meanwhile the skin residual stress under the two conditions were measured by blind hole method and the result shows that residual stress is about 270MPa in normalized status but decreases to about 70MPa after tempering.Lower yield strength may result from the high tensile residual stress in the BSS.The residual stress can be significantly decreased and the R_(0.2) of the BSS can be improved effectively after low temperature tempering.; 国家重点基础研究发展规划项目(973)(2004CB619105) |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/61316]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 王勇围,许峰云,白秉哲,等. 空冷贝氏体钢的残余应力对屈服强度的影响[J],2010, 2010. |
| APA | 王勇围.,许峰云.,白秉哲.,方鸿生.,WANG Yong-wei.,...&FANG Hong-sheng.(2010).空冷贝氏体钢的残余应力对屈服强度的影响.. |
| MLA | 王勇围,et al."空冷贝氏体钢的残余应力对屈服强度的影响".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论