| 钕掺杂对铈锆复合氧化物储氧性能的影响 | |
| 翁端 ; 王蕾 ; 吴晓东 ; 吴筱笛 ; Weng Duan ; Wang Lei ; Wu Xiaodong ; Wu Xiaodi | |
| 2010-06-10 ; 2010-06-10 | |
| 关键词 | 无机非金属材料 富锆复合氧化物 氧化钕 伪立方相 动态储氧性能 inorganic non-metallic materials Zr-rich CeO2-ZrO2 neodymia pseudo-cubic phase dynamic OSC TB321 |
| 其他题名 | Influence of neodymia doping on the oxygen storage capacity of CeO_2-ZrO_2 mixed oxides |
| 中文摘要 | 通过共沉淀法合成了不同钕(Nd)掺杂量的铈锆复合氧化物。利用XRD、BET、EPR等手段研究了Nd对铈锆复合氧化物结构影响,并评价了样品在500℃的动态和静态储放氧特性。结果表明,Nd3+离子能够进入铈锆固溶体,导致晶格扭曲,促进四方富锆相向伪立方相转变,并在一定程度上抑制铈锆的高温烧结。掺杂适量Nd后,样品的Ce3+含量增多,从而提高了新鲜及老化样品的储氧能力(OSC)。; The CeO2-ZrO2 mixed oxides with different doping amount of Nd2O3 were prepared by co-precipitation.The structure and textural properties were characterized by XRD,BET,and EPR techniques,while the OSC performance was evaluated under both dynamic and static condition at 500 ℃.The insertion of Nd into the CZ lattice causes the deformation of the crystal lattice,leads to the phase transition from tetragonal structure to pseudo cubic one.The proper doping amount of Nd introduces more Ce3+ in both the fresh and aged samples,which promotes the OSC of CZ.; 国家重点基础研究发展计划项目(2004CB719503); 国家高技术研究发展计划项目(2006AA060305) |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/61220]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 翁端,王蕾,吴晓东,等. 钕掺杂对铈锆复合氧化物储氧性能的影响[J],2010, 2010. |
| APA | 翁端.,王蕾.,吴晓东.,吴筱笛.,Weng Duan.,...&Wu Xiaodi.(2010).钕掺杂对铈锆复合氧化物储氧性能的影响.. |
| MLA | 翁端,et al."钕掺杂对铈锆复合氧化物储氧性能的影响".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论