| 低温对储氢合金及电解液性能的影响 | |
| 陈人杰 ; 李丽 ; 吴锋 ; 邱新平 ; 陈实 ; CHEN Ren-jie ; LI Li ; WU Feng ; QIU Xin-pin ; CHEN Shi | |
| 2010-06-10 ; 2010-06-10 | |
| 关键词 | 储氢合金 镍氢电池 负极材料 粉化 hydrogen-storage alloy MH/Ni batteres negative electrode material pulverization TM910 |
| 其他题名 | Effects of Low Temperature on Performance of Hydrogen-storage Alloys and Electrolyte |
| 中文摘要 | 选用镍氢动力电池负极材料储氢合金为研究对象,观察在常温、低温条件下循环后储氢合金电极表面各元素分布、粒度变化,并提出电解液电导率变化及隔膜失效也是镍氢电池早期失效的一个重要原因。实验结果表明,经低温循环失效后,合金表面一些活泼元素在电解液中发生腐蚀反应,如Co,La,Mn,Al等,其中Mn、Al溶解损失严重。合金原粉颗粒的平均大小为23.6988μm,而经25℃、-20℃下循环实验而失效的电池负极合金粉颗粒的平均粒径分别为4.1874、4.5151μm,说明负极已发生严重的粉化现象。; The hydrogen-storage alloys of Nickel/Metal hydride batteries for electric vehicle were used as the experimental materials.The elements distribution and granularity distribution of the active materials for negative electrodes were studied under the conditions of normal temperature and low temperature.The change of the electrical conductivity of electrolyte and the deterioration of diaphragm were considered to result in the degradation of Ni/MH batteries.The results showed that some active elements on the alloys were solved in the electrolyte,such as Co,La,Mn and Al.The significant loss of Mn and Al could be observed.The average size of the alloy particles of fresh battery is 23.6988 μm,while that of the batteries spent at 25℃ and-20℃ are 4.1874 μm and 4.5151 μm respectively,indicating a serious pulverization of the negative electrode.; 国家重点基础研究发展规划项目973计划(2002CB211800) |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/61035]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 陈人杰,李丽,吴锋,等. 低温对储氢合金及电解液性能的影响[J],2010, 2010. |
| APA | 陈人杰.,李丽.,吴锋.,邱新平.,陈实.,...&CHEN Shi.(2010).低温对储氢合金及电解液性能的影响.. |
| MLA | 陈人杰,et al."低温对储氢合金及电解液性能的影响".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论