	多孔β-磷酸三钙与磷灰石复合材料的制备及其细胞相容性研究
	高媛 ; 奚静 ; 董利民 ; 公衍道 ; 田杰谟 ; 赵南明 ; 张秀芳 ; GAO Yuan ; XI Jing ; DONG Li-min ; GONG Yan-dao ; TIAN Jie-mo ; ZHAO Nan-ming ; ZHANG Xiu-fang
	2010-06-10 ; 2010-06-10
关键词	β-磷酸三钙 类骨磷灰石 结构特征 生物相容性 β-tricalcium phosphate Bone-like apatite Characterization Biocompatibility R318.08
其他题名	PREPARATION AND OSTEOBLAST AFFINITY OF β-TRICALCIUM PHOSPHATE /APATITE COMPOSITES
中文摘要	综合运用三维凝胶叠层法和发泡法制备了多孔茁-磷酸三钙支架。将多孔支架在1.5倍模拟体液中浸泡14天,得到材料1;或者将其在氢氧化钠溶液中浸泡4天,再在1.5倍模拟体液中浸泡14天,得到材料2。测定了两种材料的物理性能,讨论了类骨磷灰石层对材料矿物组成及其显微结构等的影响。将两组材料分别与成骨前体细胞在体外复合培养,观察和测定了细胞的形态和增殖情况。结果表明复合材料的主要成分为茁-磷酸三钙,表面具有结构不完整的含有碳酸磷灰石的类骨磷灰石,成骨细胞能在两组材料上正常粘附和增殖,而且材料2上的细胞粘附情况更好,说明多孔茁-磷酸三钙与磷灰石的复合材料有望成为一种有应用前景的骨修复材料和骨组织工程支架材料。; A biomimetic process was developed to prepare two groups of -tricalcium phosphate/ apatite composites, sample 1 and sample 2. First, porous -tricalcium phosphate scaffold material was prepared by a multiplex method, which integrated foam technique in porous ceramics preparing and three-dimensional gel-lamination technique in rapid prototyping. Subsequent immersion in a solution with 1.5 times ion concentrations of simulated body fluid (1.5 SBF) led to the formation of sample 1. Different from sample 1, the preparation of sample 2 involved a pre-soaking of sodium hydroxide (NaOH) solution before immersion in 1.5 SBF. They were characterized by scanning electron microscopy (SEM), mercury intrusion porosimetry, wide angle X-ray diffraction (XRD) and fourier transform infrared spectroscopy (FT-IR). Further, MTT assay was used to investigate the attachment and proliferation of mouse preosteoblastic cells cultured on the composites. The cells morphology on the materials was observed by SEM. XRD and FT-IR measurements showed that two composites consisted of a normal -tricalcium phosphate structure and bone-like apatite formation on their surface. When cells were cultured on two scaffolds, no proliferation inhibition was found. Osteoblasts attachment of sample 2 was significantly better than that of sample 1 after 1 and 3 days of culture. These results suggest that two composites are promising materials for bone repairing and provide further basis for the use of -tricalcium phosphate/ apatite composite as the scaffold in bone tissue engineering.; 国家科技部“973”重大基础研究计划; 清华-裕元医学科学研究基金及清华大学基础科学基金
语种	中文 ; 中文
内容类型	期刊论文
源URL	[http://hdl.handle.net/123456789/60605]
专题	清华大学
推荐引用方式 GB/T 7714	高媛,奚静,董利民,等. 多孔β-磷酸三钙与磷灰石复合材料的制备及其细胞相容性研究[J],2010, 2010.
APA	高媛.,奚静.,董利民.,公衍道.,田杰谟.,...&ZHANG Xiu-fang.(2010).多孔β-磷酸三钙与磷灰石复合材料的制备及其细胞相容性研究..
MLA	高媛,et al."多孔β-磷酸三钙与磷灰石复合材料的制备及其细胞相容性研究".(2010).