| 混凝土结构碳化寿命的时变可靠度分析 | |
| 田冠飞 ; 安雪晖 ; 沈乔楠 ; TIAN Guan-fei ; AN Xue-hui ; SHEN Qiao-nan | |
| 2010-06-10 ; 2010-06-10 | |
| 关键词 | RC结构 混凝土碳化 钢筋锈蚀 极限状态方程 拟Monte-Carlo法 RC structure concrete carbonation reinforcing steel corrosion limit state function quasi Monte-Carlo method TU375 |
| 其他题名 | Time-dependent reliability analysis of RC structure attacked by carbonation |
| 中文摘要 | 在一般大气环境下,混凝土结构的耐久性问题主要是由于碳化引起的钢筋锈蚀问题.碳化造成混凝土结构从新建到最终失效破坏过程包括:混凝土中钢筋开始发生锈蚀;混凝土保护层开始出现顺筋裂缝;裂缝宽度达到不容许值或混凝土保护层锈胀剥落等三个阶段.采用拟Monte-Carlo随机模拟方法,计算了以上述三个状态作为极限我状态所对应的时变失效概率,计算结果令人满意.该方法可以应用于混凝土结构受钢筋腐蚀破坏的耐久性寿命预测中.; Under average air environment condition,durability deficiency of reinforced concrete structure is mainly induced by carbonation which will cause reinforcement corrosion in concrete.Usually,the failure process of RC structure from service initiation to ultimate destruction induced by carbonation can be divided into three stages: from service initiation to steel corrosion initiation;from corrosion initiation to concrete cracking initiation and from cracking to crack width up to maximum or concrete cover peeling.With quasi Monte-Carlo method,time-dependent failure probabilities corresponding to these three limit states are calculated and results are agreeable.This methodology is applicable to predict durability life-span of RC structure demolished by steel corrosion.; 国家自然科学基金资助项目(50309006) |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/60490]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 田冠飞,安雪晖,沈乔楠,等. 混凝土结构碳化寿命的时变可靠度分析[J],2010, 2010. |
| APA | 田冠飞,安雪晖,沈乔楠,TIAN Guan-fei,AN Xue-hui,&SHEN Qiao-nan.(2010).混凝土结构碳化寿命的时变可靠度分析.. |
| MLA | 田冠飞,et al."混凝土结构碳化寿命的时变可靠度分析".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论