| 电磁搅拌铝合金热模浇注温度对其凝固行为的影响 | |
| 王晶 ; 何良菊 ; 李培杰 ; Wang Jing ; He Liangju ; Li Peijie | |
| 2010-06-08 ; 2010-06-08 | |
| 关键词 | 热模浇注 电磁搅拌 A356合金 半固态 Hot Mold Pouring, Electromagnetic Stirring, A356 Alloy, Semi-solid TG249.9 |
| 其他题名 | Effects of Pouring Temperature on Solidification Behavior of Aluminum Alloy Melt with Electromagnetic Stirring |
| 中文摘要 | 将电磁搅拌后不同过热温度的A356铝合金熔体浇注到约550℃的高温铸型中制备半固态浆料。利用光学显微镜和Image-ProPlus图像分析软件对获得的浆料组织进行分析,研究了A356合金过热熔体在浇注过程中的凝固行为。结果表明,过热温度为710℃的合金熔体在随后的浇注过程中形核率小,浆料中α-Al初晶仍为发达的树枝晶组织。过热温度为670℃时合金熔体浇注时有效形核率开始大幅增加,初晶在数量和形状上逐渐由树枝晶趋向于非枝晶。过热温度为630℃的合金熔体经浇注获得的浆料组织中,平均圆整度为1.35的非枝晶在初晶中所占的比率达到约60%,晶粒平均尺寸约为30μm。; Semi-solid slurry was prepared by pouring A356 superheated melt with different temperature with electromagnetic stirring into a hot mold at 550℃. Microstructure of the prepared slurry was observed by OM ( optical microscope) and Image-Pro Plus software to understand the solidification behavior of aluminum alloy A356 superheated melt during pouring process. The results indicate that primary α-Al phase exhibits developed dendritic structure in the slurry with pouring at 710 ℃ as a result of low nucleation rate. Primary phase is converted gradually from dendrite into non-dendrite with pouring at 670 ℃ due to the great increase of effective nucleation rate in the melt. Microstructure with about 60% non-dendrite in the primary phase can be obtained with pouring at 630 ℃, in which non-dendrite with about 30 μm in size and 1.35 in roundness can be observed. |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/48404]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 王晶,何良菊,李培杰,等. 电磁搅拌铝合金热模浇注温度对其凝固行为的影响[J],2010, 2010. |
| APA | 王晶,何良菊,李培杰,Wang Jing,He Liangju,&Li Peijie.(2010).电磁搅拌铝合金热模浇注温度对其凝固行为的影响.. |
| MLA | 王晶,et al."电磁搅拌铝合金热模浇注温度对其凝固行为的影响".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论